Abstract:Titanium carbide, titanium carbonitride or titanium nitride were synthesized by a two-step carbothermic reduction method. In this method, a single-phase precursor TiCnO1-n was firstly prepared from the reaction between titanium dioxide and carbon black in argon atmosphere. Then, the precursor was used as raw materials to prepare TiN, TiCxN1-x or TiC. For the production of TiN or TiCxN1-x, the precursor was further carbothermally reduced and nitrided in nitrogen gas atmosphere. For the production of TiC, the precursor was further reduced by carbon in vacuum. In the first reduction step, it was hard to determine the precise molar ratio of TiO2:C due to the uncontrollable ratio of gaseous products CO and CO2 from TiO2 to TiCnO1-n. Whereas the second step only took place in the high temperature region and the gaseous products were thermodynamically in favor of CO. Therefore, the expected products can be obtained by precisely controlling the carbon addition after analyzing the contents of carbon and oxygen in TiCnO1-n. High purity products were prepared with good dispersivity, narrow size distribution and controllable atomic ratio of C:N. The effects of reduction temperature, reaction time, ball milling and particle sizes of raw material TiO2 were studied in detail. TiN, TiCxN1-x and TiC could be obtained under the same optimum time and temperature of 1773 K for 4 h in first step and 1873 K for 8 h in second step.

Preparation of ZrN Nanopowders by Internal Gelation and Carbothermic Nitridation

Synthesis and Characterization of Zirconium Nitride Nanopowders by Internal Gelation and Carbothermic Nitridation

Microstructure evolution and mechanism during nitridation of carbon-containing internal gelation-derived zirconia

Effect of Fructose on Preparation of Nanocrystalline Zirconium Nitride Powder by Internal Gelation Combined with Carbothermic Nitridation

Preparation Of Nanocrystalline Zirconium Carbide Powders By Carbothermal Reduction

Preparation of Zirconia Powders by Sol-gel Process

Preparation and microstructure characterization of crack-free zirconium nitride microspheres by internal gelation combined with two-step nitridation

Processing of Nanocrystalline Zirconium Carbide Powders

SYNTHESIS OF T-Zro2-tin COMPOSITE NANOPOWDERS BY SELECTIVE NITRIDATION

Effect of Carbon Powder on ZrC ZrO2 Microspheres Prepared by Internal Gelation Process

Preparation of nano-TiN powders by Ni-catalysed carbothermal reduction nitridation

From design to characterization of zirconium nitride/silicon nitride nanocomposites

A Benzene-Thermal Synthetic Route to Nanocrystalline Zrn

Hydrothermal Synthesis and Characterization of Zirconia Nanocrystallites

Preparation and Properties of CaTiO_3:Zn Nanoparticles Based on Sol-Gel Method

Preparation and characterization of NiCuZn ferrite nanocrystalline powders by auto-combustion of nitrate–citrate gels

Preparations of Titanium Nitride, Titanium Carbonitride and Titanium Carbide Via a Two-Step Carbothermic Reduction Method

The Fabrication of ZrO2–ZrC Microspheres by Internal Gelation and Carbothermal Reduction Process

Fabrication of Zirconium Nitride Nanopowder with a High Specific Surface Area by Introducing Fructose As a Double-Function Additive

Evolution of c-ZrN nanopowders in low-carbon MgO–C refractories and their properties

Improving the Ca‐assisted Urea‐Glass Method for the Synthesis of Zirconium Nitride as Potential Electrocatalyst for the Nitrogen Reduction Reaction