Abstract:Mesoporous Ce0.2Zr0.8O2 nanosized powders were synthesized via a hydrothermal method in the presence of urea without any templates using a trivalent cerium salt as the starting material. The analyses by medium-angle powder X-ray diffraction (PXRD) and vis-Raman spectroscopy showed that the Ce0.2Zr0.8O2 powders were solid solutions of pure tetragonal phase, whether as-prepared at 160degreesC or calcined at 773-1273 K. By low-angle PXRD and transmission electron microscopy, the as-prepared Ce0.2Zr0.8O2 showed a short-range ordered mesostructure probably as a result of the natural agglomeration of uniform nanoparticles upon hydrothermal treatment. The as-prepared powders had high surface areas (232-281 m(2) g(-1)) and narrow pore size distributions (3.5-4.0 nm), according to the measurements of nitrogen adsorption. After calcining at 773 K, this mesostructure was retained to some degree with lower surface areas (66-75 m(2) g(-1)) and larger pore sizes (5.1-7.2 nm). Determined by X-ray photoelectron spectroscopy, the numbers of oxygen vacancies (0.025-0.037) on the nanocrystalline surface was high for both as-prepared and calcined Ce0.2Zr0.8O2. UV-vis absorption measurements showed that the band gap energy of the as-prepared Ce0.2Zr0.8O2 nanocrystals was distinctly blue-shifted compared with the bulk value due to the quantum size effect. The catalytic tests demonstrated that the Ce0.2Zr0.8O2 nanosized powders synthesized at 160degreesC showed higher thermal stability in terms of surface area and phase composition, and higher catalytic activity for CO conversion than that synthesized at 140degreesC. Among all the catalysts tested, the mesostructured one with the highest surface area and the largest pore volume displayed the highest oxygen storage capacity of 233 mumol CO g(-1) at 773 K, and the lowest 50% conversion temperature of 641 K.

Synthesis and Pyrolysis Evolution of Glucose-Derived Hydrothermal Precursor for Nanosized Zirconium Carbide

Hydrothermal Synthesis and Characterization of Zirconia Nanocrystallites

Nanostructured Hybrid Carbon Nanotube/UltraHigh‐Temperature Ceramic Heterostructures: Microstructure Evolution and Forming Mechanism

Carbothermal Reduction Synthesis of Nanocrystalline Zirconium Carbide and Hafnium Carbide Powders Using Solution-Derived Precursors

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Processing of Nanocrystalline Zirconium Carbide Powders

Preparation Of Nanocrystalline Zirconium Carbide Powders By Carbothermal Reduction

Carbothermal synthesis of zirconium carbide hollow microspheres from polyzirconoxane and phenolic resin by spray drying

Synthesis of porous ZrC particles derived from MOF-801

Optimization of the structure and morphology of monoclinic phase nanoscale zirconium dioxide

Uniform and spherical ZrC nanoparticles derived from metal organic frameworks by one-step thermal decomposition

Synthesis, structure and porosity analysis of microporous and mesoporous carbon derived from zirconium carbide

Effects of Zr on the Precursor Architecture and High-Temperature Nanostructure Evolution of Sioc Polymer-Derived Ceramics

Preparation of Nano-ZrO2 powder via a microwave-assisted hydrothermal method

Co-precipitation of nano Mg–Y/ZrO2 ternary oxide eutectic system: Effects of calcination temperature

Synthesis and Characterization of Zirconium Nitride Nanopowders by Internal Gelation and Carbothermic Nitridation

General and facile synthesis of ceria-based solid solution nanocrystals and their catalytic properties

Non-Template Hydrothermal Route Derived Mesoporous Ce0.2zr0.8o2 Nanosized Powders With Blue-Shifted Uv Absorption And High Co Conversion Activity

Combustion Synthesis of Zirconium-Doped Ceria Nanocatalyst

Synthesis of Ultra-Fine and High-Pure Zirconium Diboride Powders Using Solution-Based Processing

The Fabrication of ZrO2–ZrC Microspheres by Internal Gelation and Carbothermal Reduction Process