Carbothermal Reduction Synthesis of Nanocrystalline Zirconium Carbide and Hafnium Carbide Powders Using Solution-Derived Precursors

Michael D. Sacks,Chang-An Wang,Zhaohui Yang,Anubhav Jain
DOI: https://doi.org/10.1023/b:jmsc.0000041702.76858.a7
IF: 4.5
2004-01-01
Journal of Materials Science
Abstract:Zirconium carbide (ZrC) and hafnium carbide (HfC) powders were produced by the carbothermal reduction reaction of carbon and the corresponding metal oxide (ZrO2 and HfO2, respectively). Solution-based processing was used to achieve a fine-scale (i.e., nanometer-level) mixing of the reactants. The reactions were substantially completed at relatively low temperatures (<1500°C) and the resulting products had small average crystallite sizes (∼50–130 nm). However, these products contained some dissolved oxygen in the metal carbide lattice and higher temperatures were required to complete the carbothermal reduction reactions. Dry-pressed compacts prepared using ZrC-based powders with ∼100 nm crystallite size could be pressurelessly sintered to ∼99% relative density at 1950°C.
What problem does this paper attempt to address?