Abstract:A series of mesoporous nanocrystalline Ce-Zr solid solutions with different Ce/Zr ratios were successfully synthesized by the evaporation-induced self-assembly strategy, and were employed as catalytic supports of CuO-based catalysts for CO oxidation. These supports and catalysts were systematically characterized by X-ray powder diffraction (XRD), N-2 physisorption, transmission electron microscopy (TEM), energy-dispersed spectroscopy (EDS) mapping, X-ray photoelectron spectroscopy (XPS), H-2 temperature programmed reduction (H2-TPR), CO2 temperature programmed desorption (CO2-TPD), etc. The catalytic performances toward CO oxidation had been carefully evaluated over these CuO-based catalysts. The effects of various influencing factors, such as the Ce/Zr ratio, mesostructure, redox properties of the support, CuO loading amount and calcination temperature, on the low-temperature catalytic activity had been carefully investigated. The results showed that the catalyst supported on the support with a Ce/Zr ratio of 80/20 exhibited the highest catalytic activity. It was also found that the Ce-Zr solid solution mesoporous catalysts exhibited much higher catalytic activity than the counterparts without evident mesostructure, demonstrating the advantages of the mesoporous catalysts by providing more accessible catalytically active sites. Besides, the mesoporous Ce-Zr solid solution-supported catalysts with excellent redox properties displayed much better catalytic performances than the commercial gamma-Al2O3-supported catalyst. The kinetic study also indicated that the apparent activation energy of the CO oxidation process was greatly affected by the Ce/Zr ratio, mesostructure, and redox properties of the support. Overall, the present CuO-based catalysts with mesoporous nanocrystalline Ce-Zr solid solutions as supports were considered as a series of promising catalysts for CO oxidation.

General and facile synthesis of ceria-based solid solution nanocrystals and their catalytic properties

Cataluminescence and Catalytic Reactions of Ethanol Oxidation over Nanosized Ce1−xZrxO2 (0 ⩽ X ⩽ 1) Catalysts

Ordered Mesoporous Ce1-xZrxO2 Solid Solutions with Crystalline Walls

Generalized and High Temperature Synthesis of a Series of Crystalline Mesoporous Metal Oxides Based Nanocomposites with Enhanced Catalytic Activities for Benzene Combustion

Non-Template Hydrothermal Route Derived Mesoporous Ce0.2zr0.8o2 Nanosized Powders With Blue-Shifted Uv Absorption And High Co Conversion Activity

Urea-Based Hydrothermally Derived Homogeneous Nanostructured Ce1-Xzrxo2 (X=0-0.8) Solid Solutions: A Strong Correlation Between Oxygen Storage Capacity and Lattice Strain

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Combustion Synthesis of Zirconium-Doped Ceria Nanocatalyst

Facile Alcohothermal Synthesis, Size-Dependent Ultraviolet Absorption, and Enhanced CO Conversion Activity of Ceria Nanocrystals

Facilely fabricating mesoporous nanocrystalline Ce–Zr solid solution supported CuO-based catalysts with advanced low-temperature activity toward CO oxidation

Dimension-Manipulated Ceria Nanostructures (0d Uniform Nanocrystals, 2d Polycrystalline Assembly, and 3d Mesoporous Framework) from Cerium Octylate Precursor in Solution Phases and Their Co Oxidation Activities

Nanocrystalline Ce1−xSmxO2−δ (x = 0.4) solid solutions: structural characterization versus CO oxidation

Influence of Ceria-Zirconia Solid Solution on Performance of Noble Metal Monolithic Oxidation Catalyst

Uniform and Porous Ce1–xZnxO2−δ Solid Solution Nanodisks: Preparation and Their CO Oxidation Activity

In-situ Formed Stable Pt Nanoclusters on Ceria-Zirconia Solid Solutions Induced by Hydrothermal Aging for Efficient Low-Temperature CO Oxidation

Mesoporous-shelled CeO2 hollow nanospheres synthesized by a one-pot hydrothermal route and their catalytic performance

A Novel Material of Ce0.7Zr0.3Ba0.1O2.1: Synthesis, Characterization and Its Catalytic Performance for CO Oxidation

Synthesis, thermal stability and catalytic activity of Ce0.72Zr0.18Pr0.1O2-δ nanodispersed solid solution in CO oxidation reaction

Facile synthesis of Pt–Ce0.63Zr0·37O2–Y catalysts and the application in catalytic oxidation of toluene

Hydrothermal synthesis and automotive exhaust catalytic performance of CeO2 nanotube arrays

Zr‐doped CeO2 Hollow slightly‐truncated nano‐octahedrons: One‐pot synthesis, characterization and their application in catalysis of CO oxidation