Abstract:Mesoporous silica-carbon nanocomposites (C-SiO2) were synthesized and used as a host carrier in carbothermal reduction to fabricate highly crystalline silicon carbide nanoparticles and nanofibers. SiC nuclei were introduced into the mesopores as seeds by infiltration of preceramic precursor polycarbosilane (PCS) prior to the heat-treatment of carbothermal reduction. X-ray diffraction, scanning electron microscopy, transmission electron microscopy, and nitrogen adsorption-desorption analysis were used to characterize C-SiO2 nanocomposites and SiC products. Crystalline SiC was not formed in the mesoporous C-SiO2 nanocomposites with a low carbon content (e.g. C/SiO2 ratio = 1.01) at 1450 degrees C. However, when a given amount of PCS was infiltrated into the mesoporous C-SiO2, SiC nanofibers and nanoparticles were produced at 1450 degrees C even in the low carbon content sample. The major morphology formed from the mesoporous C-SiO2 nanocomposites without PCS infiltration was nanoparticles, while nanofibers dominated in the products of the PCS infiltrated compositions. The results indicate that the conversion of PCS into SiC nuclei in mesopores prior to carbothermal reduction has facilitated the formation of SiC nanofibers. Therefore infiltration of seeds into mesopores of C-SiO2 precursors appears to be an effective means in accelerating the reaction and controlling of nanostructures of silicon carbide.

Syntheses and Growth Mechanisms of 3C-Sic Nanostructures from Carbon and Silicon Powders.

Synthesis and Characteristics of Cubic Silicon Carbide Nanospheres with Smooth Surfaces.

Synthesis of Silicon Carbide Nanoparticles from Carbon Nanotubes

3C-Sic Nanowires and Micro-Scaled Polyhedra: Synthesis, Characterization and Properties

Synthesis and Characterization of Carbon-Poor SiC Nanowires Via Vapor-Liquid-solid Growth Mechanism

Synthesis And Characterization Of Sio2 And Sic Micro/Nanostructures

Tuning the morphologies of SiC nanowires via the control of growth temperature, and their photoluminescence properties.

Synthesis and Characterization of SiC Nanowires Through a Reduction−Carburization Route

Synthesis and Growth Mechanism of Various SiO2 Nanostructures from Straight to Helical Morphologies

The Synthesis and Mechanism Investigations of Morphology Controllable 1-D SiCnanostructuresvia a Novel Approach

Factors Affecting the Growth of SiC Nano-whiskers

Growth and Morphology of One-Dimensional SiC Nanostructures Without Catalyst Assistant

Synthesis and Characterization of 3C and 2H-Sic Nanocrystals Starting from SiO2, C2H5OH and Metallic Mg

Iodine Assisted Low Temperature Synthesis of 3C-Sic Nanostructures and Their Formation Process.

Synthesis and Characterization of SiC Nanowires Using Silicon Evaporation

Thermal evaporation and solution strategies to novel nanoarchitectures of silicon carbide

Controlled growth of SiC crystals in combustion synthesis

A New Route of Forming Silicon Carbide Nanostructures with Controlled Morphologies

Synthesis of nanocrystalline silicon carbide powders

Formation of silicon carbide nanotubes and nanowires via reaction of silicon (from disproportionation of silicon monoxide) with carbon nanotubes.

The Synthesis Of Nanostructured Sic From Waste Plastics And Silicon Powder