Abstract:An atmosphere-assisted heating process was utilized to transform mesostructured SiC-C nanocomposites in situ into ordered mesoporous SiOC and SiCN ceramics with relatively small structural shrinkage. The mesostructured SiC-C nanocomposites were fabricated using commercially available polycarbosilane (PCS) as a ceramic precursor and mesoporous carbon CMK-3 as a hard template that itself was prepared by a nanocasting procedure from mesoporous silica SBA-15. Reactive gases including air and ammonia were employed to simultaneously incorporate O or N into SiC ceramics and oxidize or reduce the carbon template and excess carbon deposits. The procedure was carried out at 500 degrees C for 10 h and at 1000 degrees C for 10 h for air- and ammonia-assisted in situ transformations, respectively. SAXS, XRD, N-2 sorption, and TEM analyses revealed that the mesoporous SiOC and SiCN ceramics exhibit open, continuous frameworks similar to that of the primary template ordered mesoporous SBA-15. The ordered mesoporous SiOC and SiCN ceramics have high surface areas (200-400 m(2) g(-1)), large pore volumes (0.4-0.8 cm(3) g(-1)), and narrow pore size distributions (4.9-10.3 nm). The structural shrinkage from mesostructured SiC-C composites to mesoporous SiC-based ceramics decreased with increasing initial pyrolysis temperature for SiC-C nanocomposites owing to the improvement of structural rigidity. This shrinkage was found to be as low as 2.6% from mesostructured SiC-C pyrolysis at 1400 degrees C to mesoporous SiCN-1400 via ammonia-assisted in situ transformation.

Low-temperature pseudomorphic transformation of ordered hierarchical macro-mesoporous SiO2/C nanocomposite to SiC via magnesiothermic reduction.

Manipulation Of Phase And Microstructure At Nanoscale For Sic In Molten Salt Synthesis

Ordered Mesoporous SiOC and SiCN Ceramics from Atmosphere-Assisted in Situ Transformation

Low-temperature formation of nanocrystalline β-SiC with high surface area and mesoporosity via reaction of mesoporous carbon and silicon powder

Facile fabrication of three-dimensional mesoporous Si/SiC composites via one-step magnesiothermic reduction at relative low temperature

Synthesis of nanocrystalline silicon carbide powders

Direct Synthesis of Controllable Microstructures of Thermally Stable and Ordered Mesoporous Crystalline Titanium Oxides and Carbide/Carbon Composites

A New Rapid Reduction−Carbonization Route to Nanocrystalline Β-Sic

Studies of synthesizing the SiC nanometer powders by chemical vapor reaction

Synthesis and Characterization of Superconducting NbC Nanotubes

Preparation Of Nanocrystalline Silicon Carbide Powders By Carbothermal Reduction

Single-source-precursor synthesis of dense monolithic SiC/(Ti0.25Zr0.25Hf0.25Ta0.25)C ceramic nanocomposite with excellent high-temperature oxidation resistance

Novel Synthesis of (Hf0.25zr0.25ti0.25ta0.25)c-Sic Biphasic Ceramic Micro-Powders Using Single-Source-precursor Route

In-situ synthesis of nano SiC particles in Al–Si–C system at 750 °C

Densification and Enhancement of Sic Particulate Reinforced Fine Grain Sic Ceramic

Preparation of Hierarchical Porous Silicon Carbide Monoliths via Ambient Pressure Drying Sol–Gel Process Followed by High-Temperature Pyrolysis

Novel 0D-nanocarbon-silica ceramic composites: sol-gel synthesis and high-temperature evolution

Synthesis of SiC@SiO2 Nanocables Via a Catalyst-Free Carbothermal Reduction Method

Fabrication of 2H/3C-SiC heterophase junction nanocages for enhancing photocatalytic CO2 reduction

Novel Synthesis of (hf 0.25 Zr 0.25 Ti 0.25 Ta 0.25 )C-Sic Biphasic Ceramic Micro-Powders Using Single-Source-precursor Route

Molecular-Level Processing of Si-(B)-C Materials with Tailored Nano/Microstructures