Abstract:SiO2:Si:Er films were deposited on n+-Si substrate using the magnetron sputtering technique, and then Au/ SiO2: Si:Er /n+-Si diodes were fabricated. Both Er3+ photoluminescence (PL) from the SiO2: Si: Er/n+-Si and electroluminescence (EL) from the Au/SiO2: Si: Er /n+-Si diodes were studied. The 1.54 micrometers PL intensity ratio of SiO2: Si: Er/n+-Si to that of the SiO2: Er/n+-Si measured under identical conditions can be as large as ~30. While the 1.54 micrometers EL intensity ratio of an Au/ SiO2:Si:Er/n+-Si diode to that of an Au/SiO2:Er/n+-Si diode measured under identical conditions can be as large as 6. We also deposited nanoscale (SiO2:Er/Si(1.0~4.0nm)/SiO2:Er) sandwich structure, in which the silicon layer between the two SiO2:Er barriers was 1.0~4.0 nm thick with an interval of 0.2 nm, on both n+-Si and p-Si substrates. Each EL spectrum of the Au/nanoscale (SiO2:Er/Si/SiO2:Er)/n+-Si diodes can be fitted by three Gaussian bands with peak energies of 0.757 eV (1.64 micrometers ), 0.806 eV (1.54 micrometers ) and 0.860 eV (1.44 micrometers ), and full widths at half maximum of 0.052, 0.045 and 0.055 eV, respectively. Among the Au/nanoscale (SiO2:Er/Si/SiO2:Er)/n+-Si diodes with the Si layers having various thicknesses, the EL intensities of the 1.64, 1.54 and 1.44 micrometers bands of the diode with a 1.6 nm Si layer attain maxima which are 22, 8 and 7 times larger than those of the control diode without any Si layer (Au/nanoscale SiO2:Er/n+-Si), respectively.

1.53 µm photo- and electroluminescence from Er(3+) in erbium silicate.

1.53νm photo-and electroluminescence from Er3+ in erbium silicate

Correlation of Efficient Luminescence with Crystal Structures of Y-Er2si2o7 and Α-Er2si2o7 in Er-doped Silicon Oxide Films

Room temperature Er<sup>3+</sup>1.54 µm electroluminescence from Si-rich erbium silicate deposited by magnetron sputtering

Sensitized Photoluminescence of Erbium Silicate Synthesized on Porous Silicon Framework

Correlation Of Efficient Luminescence With Crystal Structures Of Y-Er2si2o7 And Alpha-Er2si2o7 In Er-Doped Silicon Oxide Films

Control of the Formation and Luminescent Properties of Polymorphic Erbium Silicates on Silicon

Photo- and electro-luminescence at 1.54 μm from Er3+ in SiC:Er2O3 films and structures

Room-Temperature Photoluminescence from Er3+ in Si-Er-O and Si-Ge-Er-O Thin Films at High Erbium Concentrations

Dependence of 1.54 Mu M Photoluminescence on Excess-Si Degrees of Er-Doped Si-Rich Sio2 Films Deposited by Magnetron Sputtering

Sensitizing Properties of Luminescence Centers on the Emission of Er3+ in Si-Rich Sio2 Film

1.54-Mu M Electroluminescence from Si-Rich Erbium Silicate

Phase Transformation and Photoluminescence Properties of Er Silicate Films by Sol-Gel Method

Enhanced Emission of Er3+ from Alternately Er Doped Si-Rich Al2o3 Multilayer Film with Si Nanocrystals As Broadband Sensitizers

ROOM-TEMPERATURE 1.54μm Er3+ PHOTOLUMINESCENCE FROM Er-DOPED SILICON-RICH SILICON OXIDE FILM GROWN BY MAGNETRON SPUTTERING

Er3+ related 1.53μm emission from Er–Si-codoped ZnO multilayer film prepared by rf-sputtering

Room-temperature Luminescence at 1.54 Μm and Other Wavelengths from Er-doped Si-rich Si Oxide

PHOTOLUMINESCENCE OF Er IN SiO x

Efficient Sensitized Photoluminescence of Er Silicate in Silicon Oxide Films Embedded with Amorphous Silicon Clusters, Part I: Fabrication

Efficient Sensitized Photoluminescence from Erbium Chloride Silicate Via Interparticle Energy Transfer

Intense Photoluminescence from Eu-doped Silicon-Rich Silicon Oxide Films Prepared by Electron Beam Evaporation