Abstract:Fe2O3-MgO/Al2O3 catalyst precursors were prepared by co-precipitation method for the growth of carbon nanotubes (CNT), and the materials were characterized by various means. The effects of reduction temperature on the surface morphology, texture properties and reduction degree of the catalysts were systematically discussed, and the effects of the catalysts on the diameter uniformity, defect degree and carbon yield of carbon nanotubes were further investigated. The results showed that the reduction temperature strongly affected the reduction degree and morphology of Fe-containing species. As the reduction temperature increased from 560 °C to 760 °C, the reduction products were (Fe2O3,Fe3O4), (Fe3O4, FexO), (FexO, Fe), (FexO, Fe), and the specific surface area tended to decrease while the pore size gradually increased, which would have a great influence on the further reduction of catalyst after C3H6 was introduced. The results showed that the best catalyst performance was achieved when the reduction temperature was 660 °C, and carbon nanotubes with a carbon yield of 1800%, graphitization degree of 0.98, diameter distribution in the range of 6~20 nm, specific surface area of 260.55 m2/g and resistivity of 52.6 mΩ·cm could be obtained, which was due to the composition and structure of the active material in the catalyst at this time were favorable for further diffusion of carbon.

Effects of the Restructuring of Fe Catalyst Films on Chemical Vapor Deposition of Carbon Nanotubes

Influence of Mesoporous Materials on the Preparation of Carbon Nanotubes

Influence of Microstructures of Fe Catalyst Film on Growth of Aligned Carbon Nanotubes

Microstructure Control of Fe Catalyst Films for the Growth of Multiwalled Carbon Nanotube Arrays

Catalysts effect on morphology of carbon nanotubes prepared by catalytic chemical vapor deposition in a nano-agglomerate bed

J2240204 Evaluation of the Properties and Alignment of Carbon Nanotube Sheet Grown by CVD Method

Study of Controlled Growth of Carbon Nanotubes in Microstructures at Low Temperature

Effect of catalyst on the growth of aligned carbon prepared by microwave chemical vapor deposition

The influence of ethanol on the growth and structure of carbon nanotubes

Effects of Temperature and Catalyst Concentration on the Growth of Aligned Carbon Nanotubes

Effect of Catalyst on Morphology of Carbon Nano-Materials Prepared in A Nano-Agglomerate Bed

Controlled Growth of Fe Catalyst Film for Synthesis of Vertically Aligned Carbon Nanotubes by Glancing Angle Deposition

Pre-heating effect on the catalytic growth of partially filled carbon nanotubes by chemical vapor deposition

Buliding microstructures of organized carbon nanotubes by chemical vapor deposition

Carbon Nanotube Synthesis and Parametric Study Using CaCO3 Nanocrystals As Catalyst Support by CVD

Chemical Vapor Deposition of Vertically Aligned Carbon Nanotube Arrays: Critical Effects of Oxide Buffer Layers

The effect of Fe and Ni catalysts on the growth of multiwalled carbon nanotubes using chemical vapor deposition

Effect of adding nickel to iron–alumina catalysts on the morphology of as-grown carbon nanotubes

How reduction temperature affects the properites of carbon nanotubes growing over Fe-MgO/Al2O3 catalyst

Modulating the Diameter of Carbon Nanotubes in Array Form Via Floating Catalyst Chemical Vapor Deposition

Thermal Analysis Study of the Growth Kinetics of Carbon Nanotubes and Epitaxial Graphene Layers on Them