Abstract:In this study, the synthesis of multi-walled carbon nanotubes (MWCNTs) was carried out by chemical vapor deposition (CVD) using propane as the carbon source and Si as the catalyst support. The effect of CVD process variables such as temperature, choice of catalyst, etc on the growth behavior of nanotubes has been examined to understand the catalytic growth of CNTs. The transition metal catalysts, Fe and Ni, were used in both elemental metal form and in a metal complex form. In the case of elemental metal catalysts, the respective metals were deposited over the Si substrate using thermal evaporation following which nanotubes were synthesized by means of CVD. Subsequent studies of the synthesized carbon nanostructures employing elemental metal catalysts revealed a significant influence of the temperature and the catalyst material on the structure of CNTs. The CNTs synthesized using Ni catalyst were bamboo-like whereas the CNTs developed employing Fe catalyst were straight tubes with partial metal filling. Consequently, growth models for the different growth mechanisms have been proposed. Certain limitations of the above process have been overcome by employing spin-coating of a metal complex catalyst material on the Si substrate. The CVD synthesis of nanotubes using metal complex catalysts always resulted in partially catalyst filled CNTs. More importantly, the metal complex catalyst could be easily patterned on the Si substrate using spin-coating and photolithography, which resulted in site selective growth of partially catalyst filled MWCNTs. Since the entire process of site selective growth is suitable for conventional device fabrication, this method is a promising and practical pathway for large-scale fabrication of several magnetic material filled CNT-based devices.

The effect of Fe and Ni catalysts on the growth of multiwalled carbon nanotubes using chemical vapor deposition

Pre-heating effect on the catalytic growth of partially filled carbon nanotubes by chemical vapor deposition

Growth and Characterization of Multi-Walled Carbon Nanotubes using Chemical Vapor Deposition

The Role of the Catalytic Particle in the Growth of Carbon Nanotubes by Plasma Enhanced Chemical Vapor Deposition

Growth temperature dependence of partially Fe filled MWCNT using chemical vapor deposition

Growth and Characterization of Bamboo-Like Multiwalled Carbon Nanotubes over Cu/Al2o3 Catalyst

Effect of adding nickel to iron–alumina catalysts on the morphology of as-grown carbon nanotubes

Carbon nanotube synthesis from propane decomposition on a pre-treated Ni overlayer

Influence of Catalyst Structures on Carbon Nanotubes Growth Via Methane-CVD

Carbon Nanotube Synthesis and Parametric Study Using CaCO3 Nanocrystals As Catalyst Support by CVD

Catalysts effect on morphology of carbon nanotubes prepared by catalytic chemical vapor deposition in a nano-agglomerate bed

Effects of Catalyst and Substrate on the Preparation of Carbon Nanotubes by ECR-CVD

Synthesis of carbon nanotubes filled with Fe3C nanowires by CVD with titanate modified palygorskite as catalyst

Effect of Nickel, Iron and Cobalt on Growth of Aligned Carbon Nanotubes

TEM Investigation on the Growth Mechanism of Carbon Nanotubes Synthesized by Hot-Filament Chemical Vapor Deposition.

Synthesis of Well-Aligned Multiwalled Carbon Nanotubes on Ni Catalyst Using Radio Frequency Plasma-Enhanced Chemical Vapor Deposition

Carbon Nanotube Growth on the Surface of Carbon Fibers by CVD

Carbon nanotubes filled partially or completely with nickel

In-situ Growth of Carbon Nano-tubes/Carbon Nano-fibers(CNTs/CNFs) on the Surface of Carbon Fibers and its Microstructure Investigation

Influence of Catalyst Thickness on Diameters of Carbon Nanotubes

CVD Growth of Carbon Nanotube Forest with Selective Wall-Number from Fe–Cu Catalyst