Abstract:Fe2O3-MgO/Al2O3 catalyst precursors were prepared by co-precipitation method for the growth of carbon nanotubes (CNT), and the materials were characterized by various means. The effects of reduction temperature on the surface morphology, texture properties and reduction degree of the catalysts were systematically discussed, and the effects of the catalysts on the diameter uniformity, defect degree and carbon yield of carbon nanotubes were further investigated. The results showed that the reduction temperature strongly affected the reduction degree and morphology of Fe-containing species. As the reduction temperature increased from 560 °C to 760 °C, the reduction products were (Fe2O3,Fe3O4), (Fe3O4, FexO), (FexO, Fe), (FexO, Fe), and the specific surface area tended to decrease while the pore size gradually increased, which would have a great influence on the further reduction of catalyst after C3H6 was introduced. The results showed that the best catalyst performance was achieved when the reduction temperature was 660 °C, and carbon nanotubes with a carbon yield of 1800%, graphitization degree of 0.98, diameter distribution in the range of 6~20 nm, specific surface area of 260.55 m2/g and resistivity of 52.6 mΩ·cm could be obtained, which was due to the composition and structure of the active material in the catalyst at this time were favorable for further diffusion of carbon.

How reduction temperature affects the properites of carbon nanotubes growing over Fe-MgO/Al2O3 catalyst

Influence of Mesoporous Materials on the Preparation of Carbon Nanotubes

Effect of support texture properties on Ni-Fe/γ-Al_2O_3 catalyst structure and catalytic performance for CO methanation

Improvement of Fe/MgO catalysts by calcination for the growth of single- and double-walled carbon nanotubes.

Effect of adding nickel to iron–alumina catalysts on the morphology of as-grown carbon nanotubes

Reduced carbon solubility in Fe nano-clusters and implications for the growth of single-walled carbon nanotubes

Synthesis Of Carbon Nanotubes By Selective Reduction Of Mixed Oxides

In Situ Carbon Nanotube Synthesis by the Reduction of NiO/γ-Al2O3 Catalyst in Methane

Catalytic Chemical Vapor Deposition of Methane to Carbon Nanotubes: Copper Promoted Effect of Ni/MgO Catalysts

Size-controlled Synthesis of Hematite -Fe2o3 Nanodisks Closed with (0001) Basal Facets and {11-20} Side Facets and Their Catalytic Performance for CO2 Hydrogenation

Catalysts effect on morphology of carbon nanotubes prepared by catalytic chemical vapor deposition in a nano-agglomerate bed

Effects of Temperature and Catalyst Concentration on the Growth of Aligned Carbon Nanotubes

Preparation of Nanosized Iron Catalyst and Small Diameter Carbon Nanotubes from Methane Decomposition

Effect of Catalyst on Morphology of Carbon Nano-Materials Prepared in A Nano-Agglomerate Bed

Porous and Lamella-like Fe/MgO Catalysts Prepared under Hydrothermal Conditions for High-Yield Synthesis of Double-Walled Carbon Nanotubes

Crystal-facet effect of γ-Al2O3 on Fe–Al2O3 catalytic performance for the co-production of hydrogen and CNTs from catalytic reforming of toluene

Microstructure Control of Fe Catalyst Films for the Growth of Multiwalled Carbon Nanotube Arrays

Temperature-sensitivity of CNTs growth from tar model compound over Ni/Al 2 O 3 with and without hydrogen addition

Fabrication of Carbon Nanotubes over Metal Catalysts Supported on Mesoporous Molecular Sieves

Suppression of methane formation as catalytic converting light hydrocarbons into H2 and carbon nanotubes

Influence of Microstructures of Fe Catalyst Film on Growth of Aligned Carbon Nanotubes