Effect of support texture properties on Ni-Fe/γ-Al_2O_3 catalyst structure and catalytic performance for CO methanation

LIU Jun,MENG Fan-hui,ZHONG Peng-zhan,JI Ke-ming,LI Zhong

2013-01-01

Abstract:Ni-Fe/γ-Al2 O3 catalysts with four different γ-Al2 O3 supports were prepared by incipient impregnation and characterized by XRD,BET and H2-TPR.Catalytic behaviors of the catalysts for low-temperature CO methanation were investigated in a slurry reactor.The results showed that the surface texture properties of γ-Al2 O3 supports had great impact on distribution of Ni reactive species and methanation activity.Moderate specific surface area(192m2/g) and pore size(5.8 nm) of γ-Al2 O3 was favor for the dispersion of active component,resulting in a higher amount of β-NiO and smaller Ni crystal particle size,which increased active sites,thus having better methanation activity and stability,with a CO conversion of 97.0% and a CH4 selectivity of 89.0%.However,the catalyst prepared by high silica γ-Al2 O3 support with larger specific surface area contained a great amount of α-NiO,which was inclined to agglomerate in the reduction process,resulting in low catalytic activity and stability,with a CO initial conversion of 85.5% and rapid deactivation after 17 hours.