Abstract:Ni-MgO dual function materials (DFMs) show promise for integrated CO2 sorption and methanation. To improve CO2 sorption capacity, Ni-MgO DFMs are promoted with alkali metal nitrates. However, the high catalyst reduction temperature will result in high energy consumption, huge temperature gap between reduction (similar to 650 degrees C) and CO2 sorption and methanation (similar to 300 degrees C), and the loss of alkali metal nitrates. In this work, we prepared a Ni/CeO2 catalyst and investigated the effect of reduction temperature on its structure-property relationships in CO2 methanation, aiming to lower the reduction temperature to an isothermal level that matches CO2 methanation. Results indicated that the reduction temperature fell from over 650 to 300 degrees C, and Ni/CeO2 reduced at 300 degrees C featured high CO2 conversion (72.7%) and CH4 selectivity (98.9%). The CO2 methanation activity of Ni/CeO2 declined significantly when the reduction temperature exceeded 400 degrees C. The formation of more oxygen vacancy defects due to the interaction between NiO and CeO2 promoted the reduction of NiO species at lower temperatures. The declined CO2 methanation activity at high reduction temperatures was ascribed to the consumption of oxygen vacancies in catalyst reduction, and less defects were available for CO2 activation and methanation. An alkali metal nitrate promoted MgO adsorbent was physically mixed with Ni/CeO2 to construct (Li-Na-K)NO3-MgO-Ni/CeO2-phy DFMs for integrated CO2 sorption and methanation. The DFMs could be facilely reduced at 300 degrees C, and this has made it possible to realize the isothermal operation of catalyst reduction and CO2 sorption and methanation in integrated CO2 capture and utilization (ICCU). The (Li-Na-K)NO3-MgO-Ni/CeO2-phy DFMs reduced at 300 degrees C exhibited an impressive CO2 uptake of 2.74 mmol CO2/g DFMs and a great CH4 yield of 1.10 mmol CH4/g DFMs, and they could be a promising alternative to Ru-based DFMs with respect to their comparable CO2 sorption capacity and methanation activity and minimized cost of raw materials.

In-Situ FTIR Study of CO2 Adsorption and Methanation Mechanism Over Bimetallic Catalyst at Low Temperature

Engineering MOx/Ni Inverse Catalysts for Low-Temperature CO2 Activation with High Methane Yields

Effect of support texture properties on Ni-Fe/γ-Al_2O_3 catalyst structure and catalytic performance for CO methanation

Insights into Nickel-Based Dual Function Materials for CO2 Sorption and Methanation: Effect of Reduction Temperature

CO2 Methanation over CoNi Bimetal-Doped Ordered Mesoporous Al2O3 Catalysts with Enhanced Low-Temperature Activities

Cobalt-doped Ni-based catalysts for low-temperature CO 2 methanation

CO2 methanation over Co Ni bimetal-doped ordered mesoporous Al2O3 catalysts with enhanced low-temperature activities

An Al2O3-supported NiFe bimetallic catalyst derived from hydrotalcite precursors for efficient CO2 methanation

Screening Transition Metals (mn, Fe, Co, and Cu) Promoted Ni-Based CO2 Methanation Bimetal Catalysts with Advanced Low-Temperature Activities

Three-dimensional porous Mn–Ni/Al2O3 microspheres for enhanced low temperature CO hydrogenation to produce methane

NiAlFe catalysts based on hydrotalcite-like precursors for low temperature CO 2 methanation: Electronic effects among components and intrinsic activity of Ni site

Influence of the Microstructure of Ni–Co Bimetallic Catalyst on CO Methanation

Enhanced sintering resistance of bimetal/SBA-15 catalysts with promising activity under a low temperature for CO methanation

NiFe and CoFe nanocatalysts supported on highly dispersed alumina-silica: Structure, surface properties, and performance in CO2 methanation

An Active Manganese Promoted Ni/Al2O3 Catalyst for Low Temperature CO2 Methanation

Research Progress and Reaction Mechanism of CO2 Methanation over Ni-Based Catalysts at Low Temperature: A Review

Highly active Ni/CeO2/SiO2 catalyst for low-temperature CO2 methanation: Synergistic effect of small Ni particles and optimal amount of CeO2

Bimetallic Ni-Co nanoparticles on SiO2 as robust catalyst for CO methanation: Effect of homogeneity of Ni-Co alloy

Insight and comprehensive study of Ni-based catalysts supported on various metal oxides for CO2 methanation

Development of Highly Stable Ni-Al 2 O 3 Catalysts for CO Methanation

Ni-based mesoporous Ce0.8Zr0.2O2 catalyst with enhanced low-temperature performance for CO2 methanation