Abstract:Ni-MgO dual function materials (DFMs) show promise for integrated CO2 sorption and methanation. To improve CO2 sorption capacity, Ni-MgO DFMs are promoted with alkali metal nitrates. However, the high catalyst reduction temperature will result in high energy consumption, huge temperature gap between reduction (similar to 650 degrees C) and CO2 sorption and methanation (similar to 300 degrees C), and the loss of alkali metal nitrates. In this work, we prepared a Ni/CeO2 catalyst and investigated the effect of reduction temperature on its structure-property relationships in CO2 methanation, aiming to lower the reduction temperature to an isothermal level that matches CO2 methanation. Results indicated that the reduction temperature fell from over 650 to 300 degrees C, and Ni/CeO2 reduced at 300 degrees C featured high CO2 conversion (72.7%) and CH4 selectivity (98.9%). The CO2 methanation activity of Ni/CeO2 declined significantly when the reduction temperature exceeded 400 degrees C. The formation of more oxygen vacancy defects due to the interaction between NiO and CeO2 promoted the reduction of NiO species at lower temperatures. The declined CO2 methanation activity at high reduction temperatures was ascribed to the consumption of oxygen vacancies in catalyst reduction, and less defects were available for CO2 activation and methanation. An alkali metal nitrate promoted MgO adsorbent was physically mixed with Ni/CeO2 to construct (Li-Na-K)NO3-MgO-Ni/CeO2-phy DFMs for integrated CO2 sorption and methanation. The DFMs could be facilely reduced at 300 degrees C, and this has made it possible to realize the isothermal operation of catalyst reduction and CO2 sorption and methanation in integrated CO2 capture and utilization (ICCU). The (Li-Na-K)NO3-MgO-Ni/CeO2-phy DFMs reduced at 300 degrees C exhibited an impressive CO2 uptake of 2.74 mmol CO2/g DFMs and a great CH4 yield of 1.10 mmol CH4/g DFMs, and they could be a promising alternative to Ru-based DFMs with respect to their comparable CO2 sorption capacity and methanation activity and minimized cost of raw materials.

Ni-based mesoporous Ce0.8Zr0.2O2 catalyst with enhanced low-temperature performance for CO2 methanation

Insights into Nickel-Based Dual Function Materials for CO2 Sorption and Methanation: Effect of Reduction Temperature

Engineering MOx/Ni Inverse Catalysts for Low-Temperature CO2 Activation with High Methane Yields

Mesoporous Ce-Zr Solid Solutions Supported Ni-based Catalysts for Low-Temperature CO2 Methanation by Tuning the Reaction Intermediates

CO<sub>2</sub> Methanation over Rare Earth Doped Ni-Based Mesoporous Ce<sub>0.8</sub>Zr<sub>0.2</sub>O<sub>2</sub> with Enhanced Low-Temperature Activity

Highly active Ni/CeO2/SiO2 catalyst for low-temperature CO2 methanation: Synergistic effect of small Ni particles and optimal amount of CeO2

CO2 methanation on Ni-Ce0.8M0.2O2 (M=Zr, Sn or Ti) catalyst: Suppression of CO via formation of bridging carbonyls on nickel

Enhanced low-temperature performance of CO2 methanation over mesoporous Ni/Al2O3-ZrO2 catalysts

CO2 Methanation over CoNi Bimetal-Doped Ordered Mesoporous Al2O3 Catalysts with Enhanced Low-Temperature Activities

CO2 methanation over Co Ni bimetal-doped ordered mesoporous Al2O3 catalysts with enhanced low-temperature activities

Screening Transition Metals (mn, Fe, Co, and Cu) Promoted Ni-Based CO2 Methanation Bimetal Catalysts with Advanced Low-Temperature Activities

Cobalt-doped Ni-based catalysts for low-temperature CO 2 methanation

Catalytic performance of Ni catalysts supported on CeO2 with different morphologies for low-temperature CO2 methanation

Enhancing the low-temperature CO2 methanation over Ni/La-CeO2 catalyst: The effects of surface oxygen vacancy and basic site on the catalytic performance

Boosting CO2 Methanation Via Tuning Metal-Support Interaction over Hollow Ni/CeO2

Niobium Modification of CeO2 Tuning Electron Density of Nickel-Ceria Interfacial Sites for Enhanced CO2 Methanation

CO2 methanation over rare earth doped Ni based mesoporous catalysts with intensified low-temperature activity

Lattice capacity-dependent activity for CO2 methanation: crafting Ni/CeO2 catalysts with outstanding performance at low temperatures

CO2 Methanation over Nickel-Based Catalysts Supported on MCM-41 with in Situ Doping of Zirconium

Antisintering and High-Activity Ni Catalyst Supported on Mesoporous Silica Incorporated by Ce/Zr for CO Methanation

Ni-CeO2 Catalyst with High Ni Loading Prepared by Salt-Assisted Solution Combustion for CO2 Methanation