Abstract:For CO2 methanation reaction, a Mg species is often utilized as the alkaline promotor for Ni based catalysts to enhance the low-temperature catalytic activity. Herein, based on a pioneer ordered mesoporous NiO-Al2O3 catalyst, a Mg alkaline promotor had been incorporated into the ordered mesoporous framework via a one-pot evaporation induced self-assembly (EISA) strategy. As a result, the ordered mesoporous NiO-MgO-Al2O3 composite oxides with Mg/Al molar ratios in a wide range (0-10%) were successfully fabricated and directly utilized as the catalysts for CO2 methanation reaction. These mesoporous catalysts were carefully characterized by X-ray diffraction, N-2 adsorption-desorption, transmission electron microscopy, selected area electron diffraction, energy dispersive spectrometer, X-ray photoelectron spectroscopy, H-2 temperature-programmed reduction, and CO2 temperature-programmed desorption measurements. It was found that the ordered mesoporous materials with large specific surface areas (180.8-232.8 m(2) g(-1)), big pore volumes (0.37-0.43 cm(3) g(-1)), and narrow pore size distributions (around 9.5 nm) could be successfully retained after the calcination at 700 degrees C. The highly dispersed Ni species were strongly interacted with the mesoporous framework in the form of NiAl2O4 spinel. The incorporation of the Mg progressively increased the surface basicity of these catalysts, which could intensify the chemisorption and activation of CO2 during the CO2 methanation reaction. Therefore, the low-temperature catalytic activity was significantly enhanced. The "volcano-shape curve" relationship between the Mg/Al molar ratio and catalytic activity had been interestingly observed, suggesting only appropriate surface basicity could obtain the optimum catalytic activity. Besides, there was no evident deactivation over these mesoporous catalysts after 50 h long-term stability tests due to the confinement effect of the mesoporous framework. Therefore, the present ordered mesoporous NiO-MgO-Al2O3 materials could be considered as a series of potential catalyst candidates for CO2 methanation.

Enhancement of magnesium aluminate-based nickel and cobalt nanostructured catalysts with iron for improved performance in carbon dioxide methanation

Effect of support texture properties on Ni-Fe/γ-Al_2O_3 catalyst structure and catalytic performance for CO methanation

Cobalt promoted Ni/MgAl2O4 catalyst in lean methane catalytic oxidation

NiFe and CoFe nanocatalysts supported on highly dispersed alumina-silica: Structure, surface properties, and performance in CO2 methanation

Optimizing CO2 methanation: effect of surface basicity and active phase reducibility on Ni-based catalysts

Investigation of the effect of cobalt on the Ni–Al2O3 catalyst prepared by the mechanochemical method for CO2 methanation

Iron promoted MOF-derived carbon encapsulated NiFe alloy nanoparticles core-shell catalyst for CO2 methanation

Insight and comprehensive study of Ni-based catalysts supported on various metal oxides for CO2 methanation

Facile preparation of a Ni/MgAl2O4 catalyst with high surface area: enhancement in activity and stability for CO methanation

Cobalt Supported Nickel Silicate Nanotubes for Efficient CO2 Methanation

Alkaline-promoted Ni based ordered mesoporous catalysts with enhanced low-temperature catalytic activity toward CO2 methanation

NiAlFe catalysts based on hydrotalcite-like precursors for low temperature CO 2 methanation: Electronic effects among components and intrinsic activity of Ni site

Effect of Modified Alumina Support on the Performance of Ni-Based Catalysts for CO2 Reforming of Methane

Cobalt-doped Ni-based catalysts for low-temperature CO 2 methanation

An Al2O3-supported NiFe bimetallic catalyst derived from hydrotalcite precursors for efficient CO2 methanation

Thermo-catalytic methane decomposition over unsupported Fe–Al and Co–Al catalysts for hydrogen and carbon nanostructures production

Facilely Fabricating Highly Dispersed Ni-based Catalysts Supported on Mesoporous MFI Nanosponge for CO2 Methanation

Ni-based Hydrotalcite-Derived Catalysts for Enhanced CO2 Methanation: Thermal Tuning of the Metal-Support Interaction

CO2 Methanation over CoNi Bimetal-Doped Ordered Mesoporous Al2O3 Catalysts with Enhanced Low-Temperature Activities

Hydrogenation of CO to methane over mesoporous nickel-iron-alumina xerogel nano-catalysts

Ni-based hydrotalcite-derived catalysts for enhanced CO 2 methanation: Thermal tuning of the metal-support interaction