Abstract:Fe2O3-MgO/Al2O3 catalyst precursors were prepared by co-precipitation method for the growth of carbon nanotubes (CNT), and the materials were characterized by various means. The effects of reduction temperature on the surface morphology, texture properties and reduction degree of the catalysts were systematically discussed, and the effects of the catalysts on the diameter uniformity, defect degree and carbon yield of carbon nanotubes were further investigated. The results showed that the reduction temperature strongly affected the reduction degree and morphology of Fe-containing species. As the reduction temperature increased from 560 °C to 760 °C, the reduction products were (Fe2O3,Fe3O4), (Fe3O4, FexO), (FexO, Fe), (FexO, Fe), and the specific surface area tended to decrease while the pore size gradually increased, which would have a great influence on the further reduction of catalyst after C3H6 was introduced. The results showed that the best catalyst performance was achieved when the reduction temperature was 660 °C, and carbon nanotubes with a carbon yield of 1800%, graphitization degree of 0.98, diameter distribution in the range of 6~20 nm, specific surface area of 260.55 m2/g and resistivity of 52.6 mΩ·cm could be obtained, which was due to the composition and structure of the active material in the catalyst at this time were favorable for further diffusion of carbon.

Influence of Mesoporous Materials on the Preparation of Carbon Nanotubes

Preparation of Carbon Nanotubes at the Surface of Fe/SBA-15 Mesoporous Molecular Sieve

Fabrication of Carbon Nanotubes over Metal Catalysts Supported on Mesoporous Molecular Sieves

The influence of ethanol on the growth and structure of carbon nanotubes

Growth of Carbon Nanotubes with Metal-Loading Mesoporous Molecular Sieves Catalysts

Influence of Cerium Metal As Catalyst on the Growth and Structure of Single-Walled Carbon Nanotubes

How reduction temperature affects the properites of carbon nanotubes growing over Fe-MgO/Al2O3 catalyst

Synthesis of carbon nanotubes filled with Fe3C nanowires by CVD with titanate modified palygorskite as catalyst

Preparation of CNTs-supported Fe3O4 and Fe3C Nano-particles and the Investigation on their Magnetic Properties

Carbon Nanotube Synthesis and Parametric Study Using CaCO3 Nanocrystals As Catalyst Support by CVD

Preparation of Nanosized Iron Catalyst and Small Diameter Carbon Nanotubes from Methane Decomposition

Influence of Microstructures of Fe Catalyst Film on Growth of Aligned Carbon Nanotubes

Effects of Temperature and Catalyst Concentration on the Growth of Aligned Carbon Nanotubes

Catalysts effect on morphology of carbon nanotubes prepared by catalytic chemical vapor deposition in a nano-agglomerate bed

Porous and Lamella-like Fe/MgO Catalysts Prepared under Hydrothermal Conditions for High-Yield Synthesis of Double-Walled Carbon Nanotubes

Carburization of Fe/Ni Catalyst for Efficient Growth of Single-Walled Carbon Nanotubes

Synthesis of Single-Walled Carbon Nanotubes with Narrow Diameter Distribution by Calcination of a Mo-Modified Fe/MgO Catalyst

Effect of Catalyst on Morphology of Carbon Nano-Materials Prepared in A Nano-Agglomerate Bed

Effect of adding nickel to iron–alumina catalysts on the morphology of as-grown carbon nanotubes

Narrow-chirality distributed single-walled carbon nanotube synthesized from oxide promoted Fe–SiC catalyst

Microstructure Control of Fe Catalyst Films for the Growth of Multiwalled Carbon Nanotube Arrays