Abstract:Single-walled carbon nanotubes (SWCNTs) with specific electrical types are urgently demanded for future nanoelectronic applications. However, it is still a challenge to simultaneously improve the purity and yield of semiconducting SWCNTs (s-SWCNTs). Herein, we propose a new multicycle approach to directly synthesize sSWCNTs by chemical vapor deposition (CVD) using Fe0.01Mg(0.99)O as catalyst regeneration host. The appropriate carbon feedstock used in the first-time growth is CH4. During this process, the lattice oxygen would be released from Fe0.01Mg0.99O catalyst through H-2 reduction and then form water vapor. The water vapor could in-situ selectively etch metallic SWCNTs (m-SWCNTs) in the nucleation process. After the termination of the firsttime growth stage, the deactivative catalyst was regenerated by oxidation treatment, then it was reused to grow SWCNTs again. Carbon feedstock was changed to C2H5OH for the multicycle growth of SWCNTs and the secondary etching of as-grown m-SWCNTs and smaller-diameter SWCNTs. The selective synthesis of s-SWCNTs through this new multicycle growth process was up to 93.2% abundance, and the yield of SWCNTs was improved from 0.76% to 1.34% (weight ratio to the catalyst powder). It is interesting that there exists a diameter threshold value, which could affect the .OH groups etching on m-SWCNTs. According to the DFT simulation, the experimental results are related to the absorption capacity and reaction activity of SWCNTs. It presents a new approach to the massive synthesis of high purity s-SWCNTs and has wide applications in the future.

Narrow-chirality distributed single-walled carbon nanotube synthesized from oxide promoted Fe–SiC catalyst

Selective growth of semiconducting single-walled carbon nanotubes solely from carbon monoxide

SiO2-promoted growth of single-walled carbon nanotubes on an alumina supported catalyst

Supported catalysts derived from cobalt phyllosilicates for chemical vapor deposition growth of single-walled carbon nanotubes

Selective Growth of Single‐walled Carbon Nanotubes using Cobalt Disilicide

Chiral-selective growth of single-walled carbon nanotubes on Fe-based catalysts using CO as carbon source

Rapid Synthesis of Fe/SiO2 Catalysts and Growth of Carbon Nanotubes by Chemical Vapor Deposition

Subnanometer Single-Walled Carbon Nanotube Growth from Fe-Containing Layered Double Hydroxides

Selective Synthesis Combined with Chemical Separation of Single-Walled Carbon Nanotubes for Chirality Selection

Selective Synthesis of Single/Double/Multi-walled Carbon Nanotubes on MgO-Supported Fe Catalyst

Carbon fiber-promoted activation of catalyst for efficient growth of single-walled carbon nanotubes

Solid supported ruthenium catalyst for growing single-walled carbon nanotubes with narrow chirality distribution

Carburization of Fe/Ni Catalyst for Efficient Growth of Single-Walled Carbon Nanotubes

Facile growth of oriented SiC nanowires arrays on carbon fiber cloth via CVD

Catalyst Design Using Nanoporous Iron for the Chemical Vapor Deposition Synthesis of Single-Walled Carbon Nanotubes

CVD Growth of Carbon Nanotube Forest with Selective Wall-Number from Fe–Cu Catalyst

A Robust CoxMg1-xO Catalyst for Predominantly Growing (6, 5) Single-Walled Carbon Nanotubes

How Catalysts Affect the Growth of Single-Walled Carbon Nanotubes on Substrates

Synthesis of Single-Walled Carbon Nanotubes with Narrow Diameter Distribution by Calcination of a Mo-Modified Fe/MgO Catalyst

Growth of Single-Walled Carbon Nanotubes with Controlled Structure: Floating Carbide Solid Catalysts

Catalyst Regeneration and Multicycle Growth of High Purity and Yield Semiconducting Single-Walled Carbon Nanotubes