Abstract:Using Fe-MgO, Co-MgO and Ni-MgO catalysts preparated by citric acid method, carbon nanotubes (CNTs) were synthesized from decomposition of methane at 873 K, 973 K and 1013 K, respectively, and were characterized by TEM and Raman spectra. The effects of catalysts, preparation temperature and reaction time on the shape, yield and inter - structure of carbon nanotubes were discussed.TEM results and Raman spectra show that the shapes and inter-structures of carbon nanotubes produced on different catalysts at the same temperature are quite different. Carbon nanotubes synthesized on Fe-MgO incline to be rods, with very thick wall, and the diameter varied greatly from 10 nm to 80 nm. However, the diameter of carbon nanotubes produced on Co-MgO is about 35 nm, and about 20 nm on Ni-MgO. As can see from the Raman spectra, the G peaks of carbon nanotubes produced on the three catalysts shift slightly, which indicate the difference of the inter-structure of nanotubes.The experiments show that the yield of carbon nanotubes varied with decomposition temperature. Using Fe-MgO catalysts, yield of carbon nanotubes grows with the decomposition temperature. However, using Ni-MgO catalysts, the yield drops when the temperature increases. The reaction temperature with the largest yield of carbon nanotubes is higher than 1013 K on Fe-MgO catalysts, about 973 K on Co-MgO catalysts, and lower than 873 K on Ni-MgO catalysts, respectively.The results also show that the yield of carbon nanotubes does not increase with the decomposition time. There is a saturation time of the carbon nanotube growth. The carbon nanotubes do not grow any more when the saturation time reaches. For example, on Ni-MgO catalysts, the carbon nanotubes stop growing after decomposition of CH4 for 2 h.

In Situ Carbon Nanotube Synthesis by the Reduction of NiO/γ-Al2O3 Catalyst in Methane

Synthesis of Carbon Nanotubes by Catalytic Chemical Vapor Deposition over Methane Reduced Ni Catalyst

Catalytic Chemical Vapor Deposition of Methane to Carbon Nanotubes: Copper Promoted Effect of Ni/MgO Catalysts

Carbon Nanotubes and Onions from Methane Decomposition Using Ni/Al Catalysts

Synthesis of Thin-Walled Carbon Nanotubes from Methane by Changing the Ni/Mo Ratio in a Ni/Mo/MgO Catalyst

In Situ Synthesis of Multiwalled Carbon Nanotubes over Lanio3 As Support of Cobalt Nanoclusters Catalyst for Catalytic Applications

Catalytic Vapor Decomposition of Methane over Nickle Catalyst: Growth Rate and the Corresponding Microstructures of Carbon Nanofibers

Synthesis of Ni and Ni–Cu Supported on Carbon Nanotubes for Hydrogen and Carbon Production by Catalytic Decomposition of Methane

The Factors of Preparation of Carbon Nanotubes by Catalytic Decomposition of Methane

Study of Preparation of Ni-Mg-O Catalysts for Growth of Carbon Nanotubes by CCVD Method

Co-production of Hydrogen and Carbon Nanotubes on Nickel Foam Via Methane Catalytic Decomposition

Promoting effects of chromium on Ni/MgO catalysts for CNTs synthesis by chemical vapor deposition method

In Situ Growth of Carbon Nanotubes on Ni/Mgo: A Facile Preparation of Efficient Catalysts for the Production of Synthetic Natural Gas from Syngas

Preparation of Nanosized Iron Catalyst and Small Diameter Carbon Nanotubes from Methane Decomposition

Enhanced Production of Carbon Nanotubes: Combination of Catalyst Reduction and Methane Decomposition

Catalytic decomposition of methane over supported Ni catalysts with different particle sizes

Synthesis Of Carbon Nanotubes By Selective Reduction Of Mixed Oxides

Reinforcing hydrogen and carbon nanotube co-production via Cr–O–Ni catalyzed methane decomposition

Fabrication and Growth Mechanism of Carbon Nanotubes by Chemical Vapor Deposition

Growth of Carbon Nanotubes by Catalytic Decomposition of CH4 or CO on a NiMgO Catalyst

A Study of CO2Methanation over Ni-Based Catalysts Supported by CNTs with Various Textural Characteristics