Abstract:Single-walled carbon nanotubes (SWCNTs) with a narrow diameter distribution and high areal density hold great promise for a variety of applications, particularly in advanced electronics and biomedical devices. This study utilizes Mn ion doping as a strategic approach both to stabilize the ZrO2-supported Fe catalyst and regulate lattice oxygen release, thereby facilitating the growth of SWCNTs with high areal density and a narrow diameter distribution. The ZrO2-supported Fe catalyst was meticulously dispersed on Si/SiO2 (300 nm) substrates through the optimization of spin-coating speed and solvent viscosity, aiming to enhance the dispersion and uniformity. Investigation into the precise control over the Mn ion content was conducted to regulate the structure and stability of the Mn-doped ZrO2-supported Fe catalyst. Mn ions perform a dual role: they maintain a higher proportion of ZrO2 in the monoclinic phase, which in turn alleviates the monoclinic-tetragonal phase transition during chemical vapor deposition (CVD) growth. Concurrently, the conversion of Mn3+ to Mn4+ ions captures the lattice oxygen released during the formation of zirconium transition oxides. Additionally, first-principles simulations have confirmed the stabilizing impact of Mn ions on the catalyst, which reduces aggregation and maturation, ultimately resulting in a more concentrated diameter distribution of as-grown SWCNTs. This approach has successfully achieved the controlled growth of high areal density SWCNTs with a diameter distribution of 1.73 +/- 0.08 nm.

Controlled Growth of Fe Catalyst Film for Synthesis of Vertically Aligned Carbon Nanotubes by Glancing Angle Deposition

Microstructure Control of Fe Catalyst Films for the Growth of Multiwalled Carbon Nanotube Arrays

Influence of Microstructures of Fe Catalyst Film on Growth of Aligned Carbon Nanotubes

Multi-Directional Growth of Aligned Carbon Nanotubes Over Catalyst Film Prepared by Atomic Layer Deposition

Thin-Film Metal Catalyst For The Production Of Multi-Wall And Single-Wall Carbon Nanotubes

Preferential Growth of Carbon Nanotubes/Nanofibers Using Lithographically Patterned Catalysts

Influence of Catalyst Film Thickness Deposited by Atomic Layer Deposition on the Growth of Aligned Carbon Nanotubes

THE GROWTH OF ALIGNED CARBON NANOTUBES ON FeNiCo CATALYST FILMS

Controlled Growth of Carbon Nanotubes on Graphite Foil by Chemical Vapor Deposition

J2240204 Evaluation of the Properties and Alignment of Carbon Nanotube Sheet Grown by CVD Method

Synthesis of Vertically-Aligned Cnt Arrays from Diameter-Controlled Fe3o4 Nanoparticles

Effect of catalyst on the growth of aligned carbon prepared by microwave chemical vapor deposition

Synthesis of Aligned Carbon Nanotubes by Thermal Chemical Vapor Deposition

Aligned carbon nanotubes growing on catalyst film prepared by spin coating

Wall-Number Selective Growth Of Vertically Aligned Carbon Nanotubes From Fept Catalysts: A Comparative Study With Fe Catalysts

Controlled Growth of Single-Walled Carbon Nanotubes with Narrow Diameter Distribution and High Areal Density on Mn-doped ZrO2-supported Fe Catalyst

Chemical Vapor Depositions of Single-Walled Carbon Nanotubes Catalyzed by Uniform Fe(2)o(3) Nanoclusters Synthesized Using Diblock Copolymer Micelles.

Growth of Carbon Nanotubes on Si Substrate Using Fe Catalyst Produced by Pulsed Laser Deposition.

Study on Diameter Controlled Growth of Carbon Nanotubes by Laal1_xfexo3 Catalysts

Controlled Growth of Single‐Walled Carbon Nanotube Films by Iron‐assisted Floating Solid Catalyst Chemical Vapor Deposition

Rapid Synthesis of Fe/SiO2 Catalysts and Growth of Carbon Nanotubes by Chemical Vapor Deposition