Abstract:Vertically aligned nitrogen-doped carbon nanotubes (NCNTs) with uniform size distribution, large aspect ratio, good orientation, and high purity were employed as novel platforms to understand the dopant-induced perturbations and found widely applications in catalysis, electrochemistry, energy conversion and storages. However, the efficient way to synthesis CNTs with ordered alignment in large scale is still a challenge. We reported NCNTs were efficiently synthesized on a lamellar vermiculite catalyst in a fluidized-bed reactor. The catalysts and as-grown products can maintain good fluidization state during the whole growth process. The intercalated growth mode prevented the NCNT arrays from the disturbance of particle collisions in the fluidized bed. With the introduction of nitrogen precursor, N atoms were doped into CNTs and formed NCNTs with bamboo-like structure. The content of N doping can be tuned in a range of 1.55–4.23% and the distribution of N-containing functional groups can also be modified by changing either the growth temperatures or nitrogen sources (NH3, 1,2-ethylenediamine, and pyridine). We explored the growth temperature ranging from 650 to 800°C. High growth temperature led to a high NCNT yield (2.95gNCNT/gcath), large NCNT diameter (about 20nm), and high graphitization degree. This provides a potential way for the controllable mass production of aligned NCNTs for applications in catalysis, materials science, energy conversion and storage, etc.

Synthesis of Vertically-Aligned Cnt Arrays from Diameter-Controlled Fe3o4 Nanoparticles

Chemical Vapor Deposition of Vertically Aligned Carbon Nanotube Arrays: Critical Effects of Oxide Buffer Layers

J2240204 Evaluation of the Properties and Alignment of Carbon Nanotube Sheet Grown by CVD Method

Rational Control on Floating Catalysts for the Growth of Carbon Nanotube Assemblies: from Vertically Aligned Carbon Nanotube Arrays to Carbon Nanotube Films

Carbon dioxide-boosted growth of high-density and vertically aligned carbon nanotube arrays on a stainless steel mesh

Integrating Vertically Aligned Carbon Nanotubes on Micromechanical Structures

Alcohol-Assisted Rapid Growth of Vertically Aligned Carbon Nanotube Arrays

Synthesis of vertically aligned CNTs with hollow channel on Al 2O3-Al substrate electroplated with Fe nanoparticles

Preferential Growth of Carbon Nanotubes/Nanofibers Using Lithographically Patterned Catalysts

Vertically aligned carbon nanotube arrays grown on a lamellar catalyst by fluidized bed catalytic chemical vapor deposition

Uniform Patterned Synthesis of Vertically-Aligned Carbon Nanotubes on Low-Stress Micromechanical Structures

Large Scale Synthesis of Vertical Aligned CNT Array on Irregular Quartz Particles

Controlled Growth of Fe Catalyst Film for Synthesis of Vertically Aligned Carbon Nanotubes by Glancing Angle Deposition

Macroscopic Three-Dimensional Arrays of Fe Nanoparticles Supported in Aligned Carbon Nanotubes

Modulating the Diameter of Carbon Nanotubes in Array Form Via Floating Catalyst Chemical Vapor Deposition

Facile Synthesis of High Density Carbon Nanotube Array by a Deposition-Growth-densification Process

Layered Growth of Aligned Carbon Nanotubes Arrays on Silicon Wafers

Efficient Synthesis of Aligned Nitrogen-Doped Carbon Nanotubes in A Fluidized-Bed Reactor

Synthesis of Vertically Aligned Carbon Nanotube Arrays on Silicon Substrates

Multi-Directional Growth of Aligned Carbon Nanotubes Over Catalyst Film Prepared by Atomic Layer Deposition

Mass Production of Aligned Carbon Nanotube Arrays by Fluidized Bed Catalytic Chemical Vapor Deposition