Abstract:The selective growth of semiconducting single-walled carbon nanotubes (s-SWCNTs) is of great importance in many high-end applications represented by nanoelectronics. Here, we developed a general approach to grow horizontally aligned s-SWCNT arrays on stable temperature (ST)-cut quartz with bimetallic catalysts using carbon monoxide (CO) as both catalyst reductant and single component carbon feedstock under atmospheric pressure. The disproportionation of CO produces not only carbon species for SWCNT growth but also CO 2 , which could act as an in-situ etchant to remove both amorphous carbon and metallic tubes. The employment of bimetallic catalyst and quartz substrate facilitates the selective etching by narrowing the diameter distribution of as-grown SWCNT arrays. At the optimized conditions, we realized the selective growth of horizontally aligned s-SWCNT arrays with the content above 97% using CoCu catalysts, confirmed by Raman characterization and electrical measurements of the fabricated field effect transistor devices. This CO-based process in selective growth of s-SWCNTs has demonstrated its feasibility and universality by the broad growth window and applicability for other bimetallic catalysts, such as FeCu and CoMn. It possesses a practical potential in obtaining semiconducting channel materials for the scalable fabrication of CNT-based devices.

Synthesis of Vertically Aligned Carbon Nanotube Arrays on Silicon Substrates

J2240204 Evaluation of the Properties and Alignment of Carbon Nanotube Sheet Grown by CVD Method

Well-aligned Carbon Nanotube Array Grown on Si-based Nanoscale SiO2 Islands

Rapid Growth of Well-Aligned Carbon Nanotube Arrays

Selective Growth of Carbon Nanotube on Silicon Substrates

Layered Growth of Aligned Carbon Nanotubes Arrays on Silicon Wafers

Synthesis of Aligned Carbon Nanotubes by Thermal Chemical Vapor Deposition

Patterned Growth of Well-aligned Carbon Nanotube Arrays on Quartz Substrates by Chemical Vapor Deposition

Controlled Growth of Metal-Free Vertically Aligned CNT Arrays on SiC Surfaces

Vertically aligned carbon nanotube arrays grown on a lamellar catalyst by fluidized bed catalytic chemical vapor deposition

Synthesis of uniformly distributed carbon nanotubes on a large area of Si substrates by thermal chemical vapor deposition

Growth of Well-Aligned Carbon Nanotube Arrays on Silicon Substrates Using Porous Alumina Film As a Nanotemplate

Substrate-Site Selective Growth of Aligned Carbon Nanotubes

Selective growth of semiconducting single-walled carbon nanotubes solely from carbon monoxide

Facile growth of oriented SiC nanowires arrays on carbon fiber cloth via CVD

Synthesis of Vertically-Aligned Cnt Arrays from Diameter-Controlled Fe3o4 Nanoparticles

Mass Production of Aligned Carbon Nanotube Arrays by Fluidized Bed Catalytic Chemical Vapor Deposition

Carbon dioxide-boosted growth of high-density and vertically aligned carbon nanotube arrays on a stainless steel mesh

Carbon nanotube arrays on silicon substrates and their possible application

Multi-Directional Growth of Aligned Carbon Nanotubes Over Catalyst Film Prepared by Atomic Layer Deposition

Large-Scale Aligned Silicon Carbonitride Nanotube Arrays: Synthesis, Characterization, and Field Emission Property