Abstract:Aligned carbon nanotubes were synthesized on Ni-coated Si substrates using microwave plasma-enhanced chemical vapor deposition. The surface morphology of Ni thin films was varied with the rf power density during the rf magnetron sputtering process. It was found that the growth of carbon nanotubes was strongly influenced by the surface morphology of Ni thin film. Pure carbon nanotubes were synthesized on Ni thin film with uniformly distributed grain sizes, whereas large amounts of carbonaceous particles were produced in addition to the nanotubes, when the nanotubes were grown on Ni thin film with widely distributed grain sizes. With decreasing Ni-grain size, the diameter of nanotubes decreased and the length increased. High-resolution transmission electron microscope images clearly demonstrated the nanotubes to be multiwalled, and the graphitized structures were confirmed from the Raman spectra. Efficient field emission was observed from the diode structure with the nanotube tips.

Synthesis of Aligned Carbon Nanotubes by Thermal Chemical Vapor Deposition

J2240204 Evaluation of the Properties and Alignment of Carbon Nanotube Sheet Grown by CVD Method

Growth Process Conditions of Vertically Aligned Carbon Nanotubes Using Plasma Enhanced Chemical Vapor Deposition

Temperature Selective Growth Of Carbon Nanotubes By Chemical Vapor Deposition

Layered Growth of Aligned Carbon Nanotubes Arrays on Silicon Wafers

PREPARATION OF ALIGNED CARBON NANOTUBES FILMS BY THERMAL CHEMICAL VAPOR DEPOSITION

Synthesis and Growth Characteristics of Well-Aligned Carbon Nanotubes by ECR-CVD

Synthesis Of Vertically Aligned Carbon Nanotubes Films On Silicon Wafers By Pyrolysis Of Ethylenediamine

Synthesis of Large Area of Aligned Carbon Nanotube by Chemical Vapor Deposition

Synthesis of Well-Aligned Multiwalled Carbon Nanotubes on Ni Catalyst Using Radio Frequency Plasma-Enhanced Chemical Vapor Deposition

Study of Controlled Growth of Carbon Nanotubes in Microstructures at Low Temperature

The Role of the Catalytic Particle in the Growth of Carbon Nanotubes by Plasma Enhanced Chemical Vapor Deposition

Uniform Patterned Growth of Carbon Nanotubes Without Surface Carbon

Growth of Aligned Carbon Nanotubes with Controlled Site Density

Preferential Growth of Carbon Nanotubes/Nanofibers Using Lithographically Patterned Catalysts

Effect of surface morphology of Ni thin film on the growth of aligned carbon nanotubes by microwave plasma-enhanced chemical vapor deposition

Growth of Aligned Carbon Nanotubes on ALD-Al2O3coated Silicon and Quartz Substrates

Synthesis of Vertically Aligned Carbon Nanotube Arrays on Silicon Substrates

Synthesis of uniformly distributed carbon nanotubes on a large area of Si substrates by thermal chemical vapor deposition

Synthesis of aligned carbon nanotube and their growth mechanism by chemical vapour deposition method

Synthesis of Aligned Carbon Nanotubes Film by Plasma-Enhanced Hot Filament Chemical Vapor Deposition