Abstract:In this study, the synthesis of multi-walled carbon nanotubes (MWCNTs) was carried out by chemical vapor deposition (CVD) using propane as the carbon source and Si as the catalyst support. The effect of CVD process variables such as temperature, choice of catalyst, etc on the growth behavior of nanotubes has been examined to understand the catalytic growth of CNTs. The transition metal catalysts, Fe and Ni, were used in both elemental metal form and in a metal complex form. In the case of elemental metal catalysts, the respective metals were deposited over the Si substrate using thermal evaporation following which nanotubes were synthesized by means of CVD. Subsequent studies of the synthesized carbon nanostructures employing elemental metal catalysts revealed a significant influence of the temperature and the catalyst material on the structure of CNTs. The CNTs synthesized using Ni catalyst were bamboo-like whereas the CNTs developed employing Fe catalyst were straight tubes with partial metal filling. Consequently, growth models for the different growth mechanisms have been proposed. Certain limitations of the above process have been overcome by employing spin-coating of a metal complex catalyst material on the Si substrate. The CVD synthesis of nanotubes using metal complex catalysts always resulted in partially catalyst filled CNTs. More importantly, the metal complex catalyst could be easily patterned on the Si substrate using spin-coating and photolithography, which resulted in site selective growth of partially catalyst filled MWCNTs. Since the entire process of site selective growth is suitable for conventional device fabrication, this method is a promising and practical pathway for large-scale fabrication of several magnetic material filled CNT-based devices.

Synthesis of uniformly distributed carbon nanotubes on a large area of Si substrates by thermal chemical vapor deposition

Transferable thin films of pristine carbon nanotubes.

Synthesis of Aligned Carbon Nanotubes by Thermal Chemical Vapor Deposition

Thin-Film Metal Catalyst For The Production Of Multi-Wall And Single-Wall Carbon Nanotubes

Uniform Patterned Growth of Carbon Nanotubes Without Surface Carbon

Selective Growth of Carbon Nanotube on Silicon Substrates

Synthesis of Vertically Aligned Carbon Nanotube Arrays on Silicon Substrates

Growth Of High-Quality Single-Wall Carbon Nanotubes Without Amorphous Carbon Formation

Study of Controlled Growth of Carbon Nanotubes in Microstructures at Low Temperature

Temperature Selective Growth Of Carbon Nanotubes By Chemical Vapor Deposition

Substrate-Site Selective Growth of Aligned Carbon Nanotubes

Growth and Characterization of Multi-Walled Carbon Nanotubes using Chemical Vapor Deposition

Synthesis and Field Emission Properties of Large-Area Uniform Carbon Nanotube Films

Layered Growth of Aligned Carbon Nanotubes Arrays on Silicon Wafers

Diameter controlled growth of single-walled carbon nanotubes from SiO2 nanoparticles

CVD Growth of N-Doped Carbon Nanotubes on Silicon Substrates and Its Mechanism

High-Density Growth of Single-Wall Carbon Nanotubes on Silicon by Fabrication of Nanosized Catalyst Thin Films

Carbon Nanotubes Synthesized by Simple Thermal Chemical Vapor Deposition and Their Electrical Properties

Narrow-chirality distributed single-walled carbon nanotube synthesized from oxide promoted Fe–SiC catalyst

TEM Investigation on the Growth Mechanism of Carbon Nanotubes Synthesized by Hot-Filament Chemical Vapor Deposition.

Low Temperature Synthesis Of High-Density Carbon Nanotubes On Insulating Substrate