Abstract:Mullite nanocomposites powders were successfully synthesized from high-aluminium coal fly ash,coal gangue,andalusite-sericite phyllite and oil shale slag through the hydrothermal crystallization process after the removal of the residual carbon,deferrization or calcination.The phase constitution and microstructure of the synthesized mullite nanocomposites powders were investigated by X-ray diffraction(XRD),transmission electron microscopy(TEM),selected area electron diffraction(SAED) and energy-dispersive X-ray(EDX).Moreover,the reaction mechanism was analyzed according to MAS-NMR results.The experimental results show that mullite nanocomposites powders can be prepared from any silicon-aluminium-bearing minerals at 80~90℃ for 3 h with NaOH concentration of 2~4 mol/L and L/S ratio(liquid/solid ratio in mass) of 10 mL/g.Mullite nanocomposites which are synthesized from coal gangue,andalusite-sericite phyllite and oil shale slag are mainly existent as whole puncheon-shaped crystals,whose average lengths are 50 nm,300 nm and 150 nm,and whose average aspect ratios are 4,3.5 and 3.75,respectively.Otherwise,when coal fly ash is used as the raw material,mullite nanocomposites are mainly rod-like,acicular and fibroid in shape with the length in the range of 30~80 nm and the diameter in the range of 4.5~30 nm.MAS-NMR analysis indicates that the nano-size mullite grows around the central atoms Al,Si of the O4 tetrahedron and the growth unit Al-4 is existent in this process definitely.

Synthesis and Controlled Growth of Mullite Submicron Powders

The Effects of Mineral Composition and Sintering Temperature on Synthetic Mullite

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Preparation of Nanocrystalline Mullite Contained Microspheres by Sol-gel Process in Oil-in-Water Emulsion

The Preparation of Mullite Nanocomposites Powders from Silicon-Aluminium- Bearing Minerals Through Hydrothermal Crystallization

Preparation of Nanometer Mullite Via Supercritical CO2

Effect of Precursor pH on One-dimensional Growth of Mullite Prepared by Sol-Gel Method with WO_3 Catalyst

Synthesis and Characterization of Ti, Fe-Doped Mullite-I

Preparation of Mullite Fibers by Sol-Gel Process and Study of Their Morphology

Synthesis of Pure-Silica Mtw Powder and Supported Films

Mullite Fibers Prepared by Sol-Gel Method Using Aluminum Chloride Aluminum Isopropoxide and Tetraethylorthosilicate

Preparation of Nanometer Mullite via Supercritical CO<sub>2</sub>

Preparation and Mechanism of Nano Mullite Powders from Kaolin Via Open Hydrothermal Process.

Effect of precursor pH on one-dimensional growth of mullite prepared by sol-gel method with WO<SUB>3</SUB> catalyst: Effect of precursor pH on one-dimensional growth of mullite prepared by sol-gel method with WO<SUB>3</SUB> catalyst

A new chemical method for preparation of both pure and doped mullite

Fabrication of ultrafine mullite powders

Fabrication and Characterization of Porous Mullite Coating on Porous Silicon Carbide Support

Preparation of Mullite Nanocomposites Powders from Coal Fly Ash Via Hydrothermal Crystallization

Preparation of Mullite Monoliths with Well-Defined Macropores and Mesostructured Skeletons Via the Sol–gel Process Accompanied by Phase Separation

Controlled Synthesis of Mesoporous Silicas Mcm-48 and Mcm-41 by Using Mixed Templates