Abstract:Mullite nanocomposites powders were successfully synthesized from high-aluminium coal fly ash,coal gangue,andalusite-sericite phyllite and oil shale slag through the hydrothermal crystallization process after the removal of the residual carbon,deferrization or calcination.The phase constitution and microstructure of the synthesized mullite nanocomposites powders were investigated by X-ray diffraction(XRD),transmission electron microscopy(TEM),selected area electron diffraction(SAED) and energy-dispersive X-ray(EDX).Moreover,the reaction mechanism was analyzed according to MAS-NMR results.The experimental results show that mullite nanocomposites powders can be prepared from any silicon-aluminium-bearing minerals at 80~90℃ for 3 h with NaOH concentration of 2~4 mol/L and L/S ratio(liquid/solid ratio in mass) of 10 mL/g.Mullite nanocomposites which are synthesized from coal gangue,andalusite-sericite phyllite and oil shale slag are mainly existent as whole puncheon-shaped crystals,whose average lengths are 50 nm,300 nm and 150 nm,and whose average aspect ratios are 4,3.5 and 3.75,respectively.Otherwise,when coal fly ash is used as the raw material,mullite nanocomposites are mainly rod-like,acicular and fibroid in shape with the length in the range of 30~80 nm and the diameter in the range of 4.5~30 nm.MAS-NMR analysis indicates that the nano-size mullite grows around the central atoms Al,Si of the O4 tetrahedron and the growth unit Al-4 is existent in this process definitely.

Preparation of Mullite Fibers by Sol-Gel Process and Study of Their Morphology

Mullite Fibers Prepared by Sol-Gel Method Using Aluminum Chloride Aluminum Isopropoxide and Tetraethylorthosilicate

Synthesis and Characterization of Rich Silica Mullite Fibers by Sol–Gel Method Using Aluminum Lactate and Silica Sol

Mullite Fibers Prepared from an Inorganic Sol–gel Precursor

Mullite Fibres Preparation by Aqueous Sol–gel Process and Activation Energy of Mullitization

The Effects of Mineral Composition and Sintering Temperature on Synthetic Mullite

Preparation of Mullite Fibres by Sol–gel Processes Using Aluminium Carboxylates and Tetraethylorthosilicate

Effect of Magnesium Oxide on Preparation of Mullite Fibers Via Sol-Gel Method

Preparation and Mullitization Kinetics of Mullite Fibres via Sol-Gel Process

A morphological study of mullite long fiber prepared using polyvinyl butyral as spinning aids

Preparation of Mullite Monoliths with Well-Defined Macropores and Mesostructured Skeletons Via the Sol–gel Process Accompanied by Phase Separation

Preparation and Thermal Stability of Zirconia-Doped Mullite Fibers Via Sol-Gel Method

Effect of the alumina and silica source mixing procedure on the microstructural evolution of alumina-mullite composite fibers prepared by sol–gel method

Preparation of Nanocrystalline Mullite Contained Microspheres by Sol-gel Process in Oil-in-Water Emulsion

Preparation of Nanometer Mullite Via Supercritical CO2

Preparation of mullite ceramics with equiaxial grains from powders synthesized by the sol-gel method

Preparation of Nanometer Mullite via Supercritical CO<sub>2</sub>

Mullite Fiber Prepared by Sol-Gel Method Using Low-Molecular-Weight Acids as Modifying Agents

Structure evolution and thermal stability of La_2O_3-doped mullite fibers via sol-gel method

Synthesis and Characterization of Electrospun Mullite Nanofibers

The Preparation of Mullite Nanocomposites Powders from Silicon-Aluminium- Bearing Minerals Through Hydrothermal Crystallization