Abstract:In this paper, the effect of phase transformation on mullite fibers' microstructure evolution and mechanical behaviors was well investigated from 1100°C to 1300°C. In such a narrow temperature range, the microstructure and mechanical properties showed great changes, which was significant to be studied. The temperature of the alumina phase transformation started below 1100°C. The main phases in the fibers were γ-Al2O3 and δ- Al2O3 with amorphous SiO2 at 1150°C. The stable α-Al2O3 formed at 1200°C. Then the mullite phase reaction occurred. As the alumina phase reaction happened, the tensile strength had been increasing with the temperature growing. In particular, the filaments achieved the highest strength at 1150°C with 1.98 ± 0.17 GPa, and the Young's modulus was 163.08 ± 4.69 GPa, showing excellent mechanical performance. After 1200°C, the mullite phase reaction went on with the crystallization of orthorhombic mullite. The density of surface defects increased rapidly due to thermal grooving, which led to mechanical properties degrade sharply. The strength at 1200°C was 1.01 ± 0.15 GPa with a strength retention of 63.13%, and the Young's modulus was 184.14 ± 10.36 GPa. While at 1300°C, the tensile strength was 0.64 ± 0.14 GPa with a strength retention of only 40.00%.This article is protected by copyright. All rights reserved

Structure evolution and thermal stability of La_2O_3-doped mullite fibers via sol-gel method

Grain boundary segregation for enhancing the thermal stability of alumina-mullite diphasic fibers by La2O3 addition

The Effects of Mineral Composition and Sintering Temperature on Synthetic Mullite

Preparation and Thermal Stability of Zirconia-Doped Mullite Fibers Via Sol-Gel Method

Preparation of Mullite Fibers by Sol-Gel Process and Study of Their Morphology

Mullite Fibers Prepared by Sol-Gel Method Using Aluminum Chloride Aluminum Isopropoxide and Tetraethylorthosilicate

Fabrication and Thermal Stability of La2O3 Doped Alumina Aerogel

Fabrication and characterization of Lal(1.8)Ca(0.2)MnO(3) nanowires

Microstructure evolution and mechanical behavior of a mullite fiber heat‐treated from 1100 to 1300°C

Effect of Magnesium Oxide on Preparation of Mullite Fibers Via Sol-Gel Method

The oriented growth behavior of α-Al2O3 grains in alumina-mullite biphasic fibers

A morphological study of mullite long fiber prepared using polyvinyl butyral as spinning aids

Effect of silica sol on phase transition of alumina-mullite fibers

Synthesis and Characterization of Ti, Fe-Doped Mullite-I

Synthesis and Characterization of Rich Silica Mullite Fibers by Sol–Gel Method Using Aluminum Lactate and Silica Sol

Crystallization Process and Microstructure of Sol–gel Derived Pb0.9La0.1Ti0.875O3 Fine Fibers with a Novel Heat-Treatment Process

Investigation of the effect of lanthanum oxide on the thermal stability of alumina aerogel

Modification of liquid phase and microstructure of sintered mullite by different additives

Raman and X-ray photoelectron spectroscopy study on the influence of La2O3 on the melt structure of SiO2–CaO–Al2O3–MgO

Effect of the alumina and silica source mixing procedure on the microstructural evolution of alumina-mullite composite fibers prepared by sol–gel method

The structural change of diphasic mullite gel studied by XRD and IR spectrum analysis