Abstract:High-strength ceramics were prepared from high alumina fly ash (HAFA) and activated alumina as raw materials with magnesia as a sintering additive. The growth kinetics and influence mechanism of secondary mullite whiskers were investigated. Meanwhile, the effects of the Al2O3/SiO2 mass ratio (A/S) and the amount of magnesia on the content and morphology of mullite in the green body were investigated, so as to emphasize the effect of the liquid phase in the sintering process on the growth of secondary mullite whiskers. The results showed that the aspect ratio of secondary mullite whiskers increased significantly after adding activated alumina to increase the A/S ratio of raw materials. When 30 wt% activated alumina was added, the mullite content increased by 5.39%, and the whisker length increased from 1.36 μm to 4.18 μm. The addition of magnesia improved the liquid phase formed during the sintering process and the K value method was used to determine the sintering liquid phase content under various conditions. It was observed that increasing the magnesia level by 1 wt% could raise the liquid phase content by 5–7%. When the total liquid content of the system was 30–40%, the growth activation energy in the diameter direction of the whisker reduced significantly, promoting the growth of secondary mullite whiskers along the C axis. The morphology of mullite gradually developed from fibrous to long columnar crystal, making it combine more densely with the green body matrix. Furthermore, the staggered long columnar mullite crystal structure changes the fracture mode of ceramics from intergranular to transgranular fracture, which fully uses the high mechanical strength of mullite. As a result, the fracture energy and strength of ceramics are significantly improved.

Preparation of mullite ceramics with equiaxial grains from powders synthesized by the sol-gel method

The Effects of Mineral Composition and Sintering Temperature on Synthetic Mullite

Preparation of Mullite Fibers by Sol-Gel Process and Study of Their Morphology

Preparation and properties of porous mullite-based ceramics fabricated by solid state reaction

Fabrication and characterization of porous mullite ceramics with ultra-low shrinkage and high porosity via sol-gel and solid state reaction methods

Preparation and Thermal Stability of Zirconia-Doped Mullite Fibers Via Sol-Gel Method

Effect Of Silica Sol On The Properties Of Alumina-Based Duplex Ceramic Cores

Effect of the alumina and silica source mixing procedure on the microstructural evolution of alumina-mullite composite fibers prepared by sol–gel method

A novel aqueous gel-casting for fabricating Al2O3-bonded fibrous mullite ceramics

Effect of silica sol on phase transition of alumina-mullite fibers

Preparation of Mullite Monoliths with Well-Defined Macropores and Mesostructured Skeletons Via the Sol–gel Process Accompanied by Phase Separation

Properties and mechanism of mullite whisker toughened ceramics

Preparation of Nanocrystalline Mullite Contained Microspheres by Sol-gel Process in Oil-in-Water Emulsion

Preparation and Characterization of Mullite Whiskers from Different Silica Sources via Molten Salt Reaction

Microstructure evolution and mechanical behavior of a mullite fiber heat‐treated from 1100 to 1300°C

Grain boundary segregation for enhancing the thermal stability of alumina-mullite diphasic fibers by La2O3 addition

Significantly improved mechanical properties of mullite ceramics by adding AlOOH with different sizes and morphologies

Preparation of monolithic transparent mullite-based glass-ceramics by the sol–gel method

Preparation of Dense Mullite Ceramics through Gelcasting of Alumina Slurry Dispersed in Silica Sol

Properties of Mullite Sol Bonded with High Aluminum Refractories

Removal of hydroxyl groups and its influence on the microstructures evolution of alumina-mullite fibers fabricated by sol-gel process