Microstructure evolution and mechanical behavior of a mullite fiber heat‐treated from 1100 to 1300°C

Wen Zhang,Xiang Yang,Ming Huang,Peng Zhi‐hang

DOI: https://doi.org/10.1111/jace.18112

IF: 4.186

2021-09-23

Journal of the American Ceramic Society

Abstract:In this paper, the effect of phase transformation on mullite fibers' microstructure evolution and mechanical behaviors was well investigated from 1100°C to 1300°C. In such a narrow temperature range, the microstructure and mechanical properties showed great changes, which was significant to be studied. The temperature of the alumina phase transformation started below 1100°C. The main phases in the fibers were γ-Al2O3 and δ- Al2O3 with amorphous SiO2 at 1150°C. The stable α-Al2O3 formed at 1200°C. Then the mullite phase reaction occurred. As the alumina phase reaction happened, the tensile strength had been increasing with the temperature growing. In particular, the filaments achieved the highest strength at 1150°C with 1.98 ± 0.17 GPa, and the Young's modulus was 163.08 ± 4.69 GPa, showing excellent mechanical performance. After 1200°C, the mullite phase reaction went on with the crystallization of orthorhombic mullite. The density of surface defects increased rapidly due to thermal grooving, which led to mechanical properties degrade sharply. The strength at 1200°C was 1.01 ± 0.15 GPa with a strength retention of 63.13%, and the Young's modulus was 184.14 ± 10.36 GPa. While at 1300°C, the tensile strength was 0.64 ± 0.14 GPa with a strength retention of only 40.00%.This article is protected by copyright. All rights reserved

materials science, ceramics