Abstract:Monotonic tensile behavior of plain-woven SiCf/SiC ceramic matrix composites is investigated at 1200 °C and 1350 °C in water–oxygen environments. In addition, tensile–tensile fatigue behavior at 1200 °C in water–oxygen environments is discussed. Specimens are prepared using chemical vapor infiltration (CVI) process. To enhance their resistance to oxidation in high-temperature water–oxygen environments, environmental barrier coatings (EBCs) are deposited on their surface. Two rows of film cooling holes (FCHs) with 0.5 mm diameter, each row consisting of five FCHs, are designed to compare the effects of two different hole spacings on specimen fatigue and tensile performance. The evolution of strain and normalized modulus during fatigue cycling is investigated in detail. Microstructures of specimens that failed under tensile and fatigue conditions are observed using scanning electron microscopy (SEM), and elemental analyses of specimens after fatigue test failure are performed using energy-dispersive spectroscopy (EDS). The results reveal that tensile strength of specimens with large FCH spacing is greater than that of specimens with small FCH spacing. However, fatigue performance of specimens with small FCH spacing was better than that of specimens with large FCH spacing. This phenomenon is caused by a reduction in strength due to stress concentration effect near holes with small FCH spacing. Holes with large FCH spacing are closer to the specimen edge during fatigue test, leading to high failure rate. The oxidation and embrittlement that surround holes caused by FCHs compromised structural integrity of the specimen and allowed water–oxygen environment to penetrate the specimen interior. This has significant impact on mechanical performance of the material.

Study of online tensile properties for continuous ceramic fibers under high‐temperature loads

High-temperature resistance and thermal insulation performance of continuous SiMOC ceramic fibers fabricated by the modified sol-gel method combined with dry spinning

Effect of thermal exposure on the microstructure and strength of an alumina‐silica ceramic fiber

Study on the Mechanical Property of High‐Performance Silicon Carbide Fiber

High-temperature tensile behavior of 3D SiC/SiC composites

Effect of heat‐treatment on the microstructure and room‐temperature mechanical properties of alumina–silica fiber

Tensile Properties of Two-Dimensional Carbon Fiber Reinforced Silicon Carbide Composites at Temperatures Up to 1800 °C in Air

Microstructure evolution and mechanical behavior of a mullite fiber heat‐treated from 1100 to 1300°C

Tensile Mechanical Behavior and Failure Mechanism of a Plain-Woven SiCf/SiC Composites at Room and Elevated Temperatures

Preparation and high-temperature properties of skin–core structure SiC ceramic fibers

Study of SiC fiber axial compressive behavior using tensile recoil measurement

Tensile Properties of Two-Dimensional Carbon Fiber Reinforced Silicon Carbide Composites at Temperatures Up to 2300 °C

The fiber structure evolution and performance changes of SiC–ZrC fibers after 1600 °C heat treatment

Microstructural and mechanical characterization of a mullite fiber

High-temperature properties of Al 2 O 3 /SiO 2 composites

Effect of long-time annealing at high temperature on the microstructure and mechanical properties of different types of SiC fibers

Tensile-tensile fatigue behavior of plain-woven SiCf/SiC ceramic matrix composites with differently spaced film cooling holes and environmental barrier coatings in high-temperature water-oxygen environments

Influence of fabric structures and temperature on the mechanical properties of quartz braids

Oxidation and mechanical properties of SiC fibers after high temperature exposure in air and steam

Evolution of strain-rate dependent compressive failure behavior of ceramifiable FRP composites at high temperature conditions

Structural evolution and mechanical properties of Cansas-III SiC fibers after thermal treatment up to 1700 °C