Abstract:Silicon carbide fiber reinforced silicon carbide composites (SiC f /SiC) are of the few most promising materials for high -temperature structural applications. In this study, two-dimensional (2D) plain -woven SiC f /SiC composites were prepared by chemical vapor infiltration process and subjected to single -sided notched beam three-point bending tests from room temperature (RT) to 1500 degrees C in air. The temperature -dependent bending load -deflection curves and fracture toughness were obtained. The results show that the SiC f /SiC composites exhibit linear deformation characteristics initially, followed by nonlinear deformation behavior which become more pronounced with increasing temperature. The fracture toughness decreases in the range of RT to 1000 degrees C due to the evolution of components properties, and increases at 1200 degrees C due to the interface property degradation and fiber pull-out. Above 1200 degrees C, it decreases with increasing temperature owing to the serious hightemperature oxidation. Further, the failure mechanisms of the 2D plain -woven SiC f /SiC composites at different temperatures was analyzed through macro and micro analysis. The evolution of components properties affected by high temperature and oxidation as well as fiber pull-out play a leading role in fracture toughness of composites. The findings of this study provide important support for the mechanical behavior and failure mechanisms of SiC f /SiC composites at ultra -high temperatures in air.

Tensile Properties of Two-Dimensional Carbon Fiber Reinforced Silicon Carbide Composites at Temperatures Up to 1800 °C in Air

Tensile Properties of Two-Dimensional Carbon Fiber Reinforced Silicon Carbide Composites at Temperatures Up to 2300 °C

Fracture Toughness Evolution and Failure Mechanisms of Two-Dimensional SiCf/SiC Composites at Temperatures Up to 1500 °C in Air

Tensile Properties of 2D-C/sic Composites at Temperatures Up to 1873 K at Wide-Ranging Strain Rates

Mechanical Behavior of 2D C/SiC Composites at Elevated Temperatures under Uniaxial Compression

Experimental Study of High-Temperature Tensile Mechanical Properties of 3D Needled C/C–SiC Composites

Insights into Fracture Mechanisms and Strength Behaviors of Two-Dimensional Carbon Fiber Reinforced Silicon Carbide Composites at Elevated Temperatures

High-temperature tensile behavior of 3D SiC/SiC composites

The Dynamic Tensile Properties of 2D-C/sic Composites at Elevated Temperatures

High temperature bending properties and failure mechanism of 3D needled C/SiC composites up to 2000 °C

An Investigation of Dynamic Failure Progress and Properties of 2D C/SiC Composite from 173 K to 1273 K by SHTB

Tensile Fatigue of a 2.5D-C/sic Composite at Room Temperature and 900°C

Tensile Mechanical Behavior and Failure Mechanism of a Plain-Woven SiCf/SiC Composites at Room and Elevated Temperatures

Compressive Behavior of C/SiC Composites over a Wide Range of Strain Rates and Temperatures

Compressive Behaviors of Continuous Carbon Fiber Reinforced Silicon Carbide Composites at High Temperature and High Strain Rate

Thermal Expansion Behavior of Carbon Fiber Reinforced Chemical-Vapor-infiltrated Silicon Carbide Composites from Room Temperature to 1400 °C

Mechanical Behaviors of C/SiC Composites Subjected to Uniaxial Compression at High Temperatures and High Strain Rates

Flexural Properties of Carbon-Carbon Composites at Temperatures Up to 2600 °C

Tensile Behavior of 2D-C/sic Composites at Elevated Temperatures: Experiment and Modeling

Compressive Strength and Damage Mechanisms of 2D-C/sic Composites at High Temperatures

The Effects of Crossover Pores on High Temperature Bending Behavior of 3-Dimensional Braided C/Sic