Abstract:This study objective is a proposal of a new lightweight and affordable structural material with heat resistance of 600–1000°C. We developed process technology and evaluated the mechanical properties of SiC fiber (Hi‐Nicalon)/Si‐CoSi2 matrix composites. After Hi‐Nicalon fibers were woven into orthogonal three‐dimensional fabrics (Vf 40%), a carbon layer (FB‐C) was formed on the fiber surface using film boiling, serving as the fiber–matrix interface layer. To suppress Hi‐Nicalon strength degradation, Si‐22 at.% Co alloy with a lower melting point compared to pure Si was infiltrated at 1380°C to produce Hi‐Nicalon/FB‐C/Si‐CoSi2 matrix composites. Dense composites with no open pores were obtained. Their bulk density was 2.7 g/cm3. Their mean value of four‐point bending strength was 460 MPa at room temperature and 612 MPa at 800°C in an Argon atmosphere. Fiber pullout and fiber bridging were observed clearly on the fracture surfaces. The FB‐C, with an average thickness of 4 μm, suppresses Hi‐Nicalon damage from the molten Si‐Co alloy. Furthermore, an inexpensive oxidation‐resistant coating of Si‐Co alloy dispersed with TiB2 and SiC particles was formed on the composite surface. The four‐point bending strength in air was 424 MPa at 800°C and 539 MPa at 1200°C, demonstrating that the oxidation‐resistant coating functions effectively.

Thermophysical and Mechanical Properties of A Three-Dimensional Hi-Nicalon/Sic Composite

Influence of SiC Coating Thickness on Mechanical Properties of SiCf/SiC Composite

Thermal Expansion Behavior of Carbon Fiber Reinforced Chemical-Vapor-infiltrated Silicon Carbide Composites from Room Temperature to 1400 °C

Oxidation behavior of 3D Hi–Nicalon/SiC composite

High-temperature tensile behavior of 3D SiC/SiC composites

Tensile Properties of Two-Dimensional Carbon Fiber Reinforced Silicon Carbide Composites at Temperatures Up to 1800 °C in Air

Tensile Properties of Two-Dimensional Carbon Fiber Reinforced Silicon Carbide Composites at Temperatures Up to 2300 °C

High temperature bending properties and failure mechanism of 3D needled C/SiC composites up to 2000 °C

Bending and Thermal Expansion Properties of 3D-C_f/sic Composites

EFFECTS OF FABRIC ARCHITECTURES ON THE THERMAL EXPANSION COEFFICIENT AND THE THERMAL DIFFUSIVITY OF CARBON FIBER REINFORCED SILICON CARBIDE COMPOSITES

Mechanical properties of SiC fiber/carbon/Si‐Co matrix composites processed using film boiling and melt infiltration

Bending and Thermal Expansion Properties of 2.5D C/SiC Composites

Computational Study of the Nanoscale Mechanical Properties of C-S-H Composites under Different Temperatures

High-Temperature Properties of SiC-Si3N4 Particle Composites

High-temperature constitutive model for three-dimensional needled C/C-SiC composite under tensile loading

Cf/SiC Ceramic Matrix Composites with Extraordinary Thermomechanical Properties up to 2000 °C

Fluoride doped SiC/Si3N4 composite as a high thermal conductive material with enhanced mechanical properties

A high-temperature structural and wave-absorbing SiC fiber reinforced Si3N4 matrix composites

Tensile Mechanical Behavior and Failure Mechanism of a Plain-Woven SiCf/SiC Composites at Room and Elevated Temperatures

Effects of Interphase Thickness and Heat Treatment on Transverse Thermal Diffusivity of 3 D C / SiC Composites

Microstructure and mechanical properties of SiC fiber/Si-CoSi2 matrix composites fabricated by carbon chemical vapor infiltration and Si alloy melt infiltration process