Abstract:SiC/SiC composites, prepared by reactive melt infiltration (RMI), exhibit exceptional properties. However, the presence of residual Si in the composite matrix can significantly compromise their high-temperature mechanical properties. Addressing the issue of high-content residual Si aggregation remains a crucial focus of research in order to fully unlock the application potential of SiC/SiC composites prepared by RMI. In this work, a special porous carbon (C g ) is successfully synthesized and introduced into the porous 2D SiC/SiC composites prepared by CVI. The unique pore structure of the SiC/SiC-C g is thoroughly analyzed, along with its liquid Si infiltration process. The difference in coefficient of thermal expansion (CTE) between SiC and C g can cause thermal stress, which can destory the C g structure. Consequently, the C particles detach from the C g skeleton and react with liquid Si to create SiC. This process effectively separates residual Si and helps alleviate the negative effects of residual Si aggregation. The microstructure and phase distribution of SiC/SiC composites obtained by liquid Si infiltrating different C structures are investigated and compared, and it demonstrates the positive effect of C g on the uniform phase distribution of matrix in the composites. The as-received SiC/SiC composites possess a density of 2.94 g/cm 3 with open porosity of 1.23%, and a flexural strength of 808.7±10.2MPa, a fracture toughness of 25.5±1.8MPa·m 1/2 , a tensile strength of 317.4±12.4MPa and a proportional ultimate stress of 157.33±4.1MPa. Acoustic emission (AE) and digital image correlation (DIC) technology are used to study the special mechanical behavior of composites.

Bending and Thermal Expansion Properties of 2.5D C/SiC Composites

Bending and Thermal Expansion Properties of 3D-C_f/sic Composites

Influence of SiC Coating Thickness on Mechanical Properties of SiCf/SiC Composite

Thermal Expansion Behavior of Carbon Fiber Reinforced Chemical-Vapor-infiltrated Silicon Carbide Composites from Room Temperature to 1400 °C

Influence of Reinforcement with Multimodal Distribution on Thermophysical Properties and Fracture Behavior in Al-Si/SiC Composites Infiltrated under Super-Gravity Field

High temperature bending properties and failure mechanism of 3D needled C/SiC composites up to 2000 °C

EFFECTS OF FABRIC ARCHITECTURES ON THE THERMAL EXPANSION COEFFICIENT AND THE THERMAL DIFFUSIVITY OF CARBON FIBER REINFORCED SILICON CARBIDE COMPOSITES

In-situ synthesis and microstructural evolution of a SiC reinforced Al-50Si composite exhibiting exceptional thermal properties

Comparison of Test Results and Finite-Element Analysis Using Elastoplastic Modeling of 2.5D C/SiC Composites

Thermophysical and Mechanical Properties of A Three-Dimensional Hi-Nicalon/Sic Composite

The Thermal Expansion Behaviour of SiCp/Al–20Si Composites Solidified under High Pressures

Mechanical and thermal expansion behavior of hybrid aluminum matrix composites reinforced with SiC particles and short carbon fibers

Tensile Properties of Two-Dimensional Carbon Fiber Reinforced Silicon Carbide Composites at Temperatures Up to 1800 °C in Air

Microstructure, mechanical properties and thermal conductivity of (Ti0.5Nb0.5)C–SiC composites

Predictions of elastic property on 2.5D C/SiC composites based on numerical modeling and semi-analytical method

Influence of High-Temperature Oxidation and Test Conditions on the Dynamic Mechanical Properties of 2.5D SiCf/SiCm Composites

Tensile Properties of Two-Dimensional Carbon Fiber Reinforced Silicon Carbide Composites at Temperatures Up to 2300 °C

High-temperature tensile behavior of 3D SiC/SiC composites

A novel porous carbon synthesized to serve in the preparation of highly dense and high-strength SiC/SiC by reactive melt infiltration

Effect of chemical vapor infiltration on the flexural properties of C/C-SiC composites prepared by the precursor infiltration pyrolysis method

Improving mechanical and thermal expansion properties of aluminum matrix composites reinforced by silicon carbide fiber