Abstract:Al/SiC composites with volume fractions of SiC between 0.55 and 0.71 were made from identical tapped and vibrated powder preforms by squeeze casting (SC) and by two different setups for gas pressure infiltration (GPI), one that allows short (1–2 min) liquid metal/ceramic contact time (fast GPI) and the other that operates with rather long contact time, i.e., 10–15 min, (slow GPI). Increased liquid metal–ceramic contact time is shown to be the key parameter for the resulting thermal and electrical conductivity in the Al/SiC composites for a given preform. While for the squeeze cast samples neither dissolution of the SiC nor formation of Al4C3 was observed, the gas pressure assisted infiltration led inevitably to a reduced electrical and thermal conductivity of the matrix due to partial decomposition of SiC leading to Si in the matrix. Concomitantly, formation of Al4C3 at the interface was observed in both sets of gas pressure infiltrated samples. Longer contact times lead to much higher levels of Si in the matrix and to more Al4C3 formation at the interface. The difference in thermal conductivity between the SC samples and the fast GPI samples could be rationalized by the reduced matrix thermal conductivity only. On the other hand, in order to rationalize the thermal conductivity of the slow GPI a reduction in the metal/ceramic interface thermal conductance due to excessive Al4C3-formation had to be invoked. The CTE of the composites generally tended to decrease with increasing volume fraction of SiC except for the samples in which a large expansive drift was observed during the CTE measurement by thermal cycles. Such drift was essentially observed in the SC samples with high volume fraction of SiC while it was much smaller for the GPI samples.

The Thermal Expansion Behaviour of SiCp/Al–20Si Composites Solidified under High Pressures

High pressure sintering behavior and mechanical properties of cBN-Ti 3Al and cBN-Ti 3Al-Al composite materials

Influence of Reinforcement with Multimodal Distribution on Thermophysical Properties and Fracture Behavior in Al-Si/SiC Composites Infiltrated under Super-Gravity Field

Mechanical and thermal expansion behavior of hybrid aluminum matrix composites reinforced with SiC particles and short carbon fibers

Interfacial Regulation and Fracture Mechanism of Al–Si/SiC Composites Infiltrated under Super-Gravity Field

Nano-Phase and SiC–Si Spherical Microstructure in SiC/Al-50Si Composites Solidified under High Pressure

Tailoring the thermophysical properties of porous SiC framework reinforced Al-Mg-Si composites by Si alloying content for thermal energy management

Thermal Expansion Behavior of Carbon Fiber Reinforced Chemical-Vapor-infiltrated Silicon Carbide Composites from Room Temperature to 1400 °C

Effects of SiC contents on the microstructure and mechanical properties of Al4SiC4–SiC ceramic composites

Improving mechanical and thermal expansion properties of aluminum matrix composites reinforced by silicon carbide fiber

In-situ synthesis and microstructural evolution of a SiC reinforced Al-50Si composite exhibiting exceptional thermal properties

Forming process of hot-extruded SiCw/6061AI composites(I)

Influence of processing route on electrical and thermal conductivity of Al/SiC composites with bimodal particle distribution

Pressure Sintering, Structure and Some Properties of SiC–Al Composite Materials

Aging and Thermal Expansion Behavior of Si3N4p/2024Al Composite Fabricated by Pressure Infiltration Method

Pressureless Sintering and High-Temperature Strength of SiC-AlN Ceramics

In-plane thermal expansion behavior of dense ceramic matrix composites containing SiBC matrix

Bending and Thermal Expansion Properties of 2.5D C/SiC Composites

Enhanced Mechanical Properties of SiC/Al Composites at Cryogenic Temperatures

Micromechanics-based thermal expansion characterization of SiC nanoparticle-reinforced metal matrix nanocomposites

Effect of Ti Doping on the Microstructure and Properties of SiCp/Al Composites by Pressureless Infiltration