Cf/SiC Ceramic Matrix Composites with Extraordinary Thermomechanical Properties up to 2000 °C

Min-sung Park,Jian Gu,Heesoo Lee,Sea-Hoon Lee,Lun Feng,William G. Fahrenholtz

DOI: https://doi.org/10.3390/nano14010072

IF: 5.3

2023-12-26

Nanomaterials

Abstract:The thermomechanical properties of carbon fiber reinforced silicon carbide ceramic matrix composites (Cf/SiC CMCs) were studied up to 2000 °C using high-temperature in situ flexural testing in argon. The CMC specimens were fabricated using an ultrahigh concentration (66 vol%) aqueous slurry containing nano-sized silicon carbide powder. The SiC powder compacts were obtained by drying the slurry and were densified using the precursor impregnation and pyrolysis (PIP) method with field assisted sintering technology/spark plasma sintering (FAST/SPS). The high relative density of the SiC green body (77.6%) enabled densification within 2.5 days using four PIP cycles. In contrast, conventional PIP processes take over 7 days. The in situ flexural strength of the Cf/SiC CMC was 434 MPa at 1750 °C, which was 84% higher than the room temperature value. The value further increased to 542 MPa at 2000 °C. Possible mechanisms to explain the excellent strength of the CMC at elevated temperatures are discussed.

materials science, multidisciplinary,physics, applied,nanoscience & nanotechnology,chemistry

What problem does this paper attempt to address?

The paper aims to address the mechanical performance issues of carbon fiber reinforced silicon carbide ceramic matrix composites (Cf/SiC CMCs) at high temperatures. Specifically, the study successfully prepared Cf/SiC composites with excellent high-temperature mechanical properties by using high-concentration slurry and precursor infiltration pyrolysis (PIP) methods. The core objective of the paper is to evaluate the high-temperature performance of this composite material through high-temperature in-situ bending tests in an argon environment and to explore the mechanisms of its high-strength characteristics under extreme temperature conditions (up to 2000°C).

Key points of the study include:
1. **Material Preparation**: High-density SiC matrix was prepared using ultra-concentrated slurry (solid content up to 66 vol%) and PIP technology.
2. **Performance Testing**: In-situ bending strength tests were conducted at high temperatures (1750°C and 2000°C), and the results showed that the material's strength reached 542MPa at 2000°C, which is significantly higher than its strength at room temperature.
3. **Mechanism Analysis**: The study explored the possible mechanisms for maintaining high strength of the composite at high temperatures, particularly the thermal stability of nano-scale SiC fillers and their role in inhibiting crack propagation.

In summary, the paper mainly focuses on how to improve the mechanical performance of Cf/SiC composites under extreme high-temperature conditions by enhancing the material preparation process and reveals the specific mechanisms to achieve this goal.