Abstract:Abstract Finding the optimum balance between strength and toughness, as well as acquiring reliable thermal shock resistance and oxidation resistance, has always been the most concerned topic in the discussion of ultra-high temperature ceramic composites. Herein, PyC modified 3D carbon fiber is used to reinforce ultra-high temperature ceramic (UHTC). The macroscopic block composite with large size is successfully fabricated through low temperature sintering at 1300 °C without pressure. The prepared PyC modified 3D C f /ZrC-SiC composites simultaneously possess excellent physical and chemical stability under the synergistic effect of PyC interface layer and low temperature sintering without pressure. The fracture toughness is increased in magnitude to 13.05 ± 1.72 MPa·m 1/2 accompanied by reliable flexural strength of 251 ± 27 MPa. After rapid thermal shock spanning from room temperature (RT) to 1200 °C, there are no visible surface penetrating cracks, spalling, or structural fragmentation. The maximum critical temperature difference reaches 875 °C, which is nearly three times higher than that of traditional monolithic ceramics. The haunting puzzle of intrinsic brittleness and low damage tolerance are resolved fundamentally. Under the protection of PyC interface layer, the carbon fibers around oxide layer and matrix remain structure intact after static oxidation at 1500 °C for 30 min. The oxide layer has reliable physical and chemical stability and resists the erosion from fierce oxidizing atmosphere, ensuring the excellent oxidation resistance of the composites. In a sense, the present work provides promising universality in designability and achievement of 3D carbon fiber reinforced ceramic composites.

From Ferroconcrete to Cf/UHTC-SiC: A Totally Novel Densification Method and Mechanism at 1300 °C Without Pressure

Interfacial Regulation and Fracture Mechanism of Al–Si/SiC Composites Infiltrated under Super-Gravity Field

Efficient fabrication and properties of 2D Cf/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C-SiC high-entropy ceramic matrix composites via slurry infiltration lamination combined with precursor infiltration and pyrolysis

Fabrication, Microstructural Evolution, and Mechanical Properties of SiC/(Hf0.25Ta0.25Zr0.25Nb0.25)C/C Nanocomposites

Effect of SiC on the anti-ablation resistance and flexural strength of (Hf-Ta-Zr)C-C/C composites

Reactive sintering of 2.5D Cf/ZrC-SiC ceramic matrix composite

Enhanced mechanical properties and thermal shock resistance of Cf/ZrB2-SiC composite via an efficient slurry injection combined with vibration-assisted vacuum infiltration

Densification and Enhancement of Sic Particulate Reinforced Fine Grain Sic Ceramic

Enhanced strength and toughness of SiC/C composite ceramics via SiC@graphene core–shell nanoparticles

Cf/SiC Ceramic Matrix Composites with Extraordinary Thermomechanical Properties up to 2000 °C

A novel porous carbon synthesized to serve in the preparation of highly dense and high-strength SiC/SiC by reactive melt infiltration

Processing, microstructure, and mechanical properties of chopped SiC fibers reinforced ZrB2–hBN–based composites

Enhancing densification rate and the unusual 4H-SiC polytype stabilization in ultrafast high-temperature sintering of α-SiC

SiC fiber strengthened Si 14Ti high-temperature filler alloy for brazing SiC f /SiC and C/C composites

Novel (Zr, Ti)(C, N)–SiC ceramics via reactive hot-pressing at low temperature

Microstructures and Enhanced Mechanical Properties of (Zr, Ti)(C, N)-Based Nanocomposites Fabricated by Reactive Hot-Pressing at Low Temperature

Fabrication and microstructure evolution of Csf/ZrB2-SiC composites via direct ink writing and reactive melt infiltration

Fabrication of dense Cf/SiC ceramic matrix composites using 3D printing and PIP with short carbon fibre as a toughening material

Using PyC modified 3D carbon fiber to reinforce UHTC under low temperature sintering without pressure

Cr3C2 assisted ultrafast high-temperature sintering of TiC

Densification mechanism, microstructure and mechanical properties of ZrC ceramics prepared by high-pressure spark plasma sintering