Abstract:In this study, continuous carbon reinforced Cf/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C–SiC high entropy ceramic matrix composites were additively manufactured through paper laminating (PL), direct slurry writing (DSW), and precursor infiltration and pyrolysis (PIP). (Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C high entropy ceramic (HEC) powders were synthesized by pressureless sintering and ball milling. A certain proportion of HEC powder, SiC powder, water, binder, and dispersant were mixed to prepare the HEC-SiC slurry. Meanwhile, BN coating was prepared on the 2D fiber cloth surface by the boric acid-urea method and then the cloth was cut into required shape. Additive manufacturing were conducted subsequently. Firstly, one piece of the as-treated carbon fiber cloth was auto-placed on the workbench by paper laminating (PL). Then, the HEC-SiC slurry was extruded onto the surface of the cloth by direct slurry writing (DSW). PL and DSW process were repeated, and a Cf/HEC-SiC preform was obtained after 3 cycles. At last, the preform was densified by precursor infiltration and pyrolysis (PIP) and the final Cf/HEC-SiC composite was prepared. The open porosity of the Cf/HEC-SiC composites, with the HEC volume fractions of 15, 30 and 45%, were 7.7, 10.6, and 11.3%, respectively. And the density of the Cf/HEC-SiC composites, with the HEC volume fractions of 15, 30 and 45%, were 2.9, 2.7 and 2.3 g/cm3, respectively. The mechanical properties of the Cf/HEC-SiC composites increased firstly and then decreased with the HEC content increase, reaching the maximum value when the HEC volume fraction was 30%. The mechanical properties of the Cf/HEC-SiC composites containing 45, 30 and 15% HEC were as follows: flexural strength (180.4 ± 14 MPa, 183.7 ± 4 MPa, and 173.9 ± 4 MPa), fracture toughness (11.9 ± 0.17 MPa m1/2, 14.6 ± 2.89 MPa m1/2, and 11.3 ± 1.88 MPa m1/2), and tensile strength (71.5 ± 4.9 MPa, 98.4 ± 12.2 MPa, and 73.4 ± 8.5 MPa). From this study, the additive manufacturing of continuous carbon fiber reinforced high entropy ceramic matrix composites was achieved, opening a new insight into the manufacturing of ceramic matrix composites.

Efficient fabrication and properties of 2D Cf/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C-SiC high-entropy ceramic matrix composites via slurry infiltration lamination combined with precursor infiltration and pyrolysis

Low temperature fabrication of Cf/BNi/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C-SiCm high entropy ceramic matrix composite by slurry coating and laminating combined with precursor infiltration and pyrolysis

Additive manufacturing of continuous carbon fiber reinforced high entropy ceramic matrix composites via paper laminating, direct slurry writing, and precursor infiltration and pyrolysis

Fabrication, Microstructural Evolution, and Mechanical Properties of SiC/(Hf0.25Ta0.25Zr0.25Nb0.25)C/C Nanocomposites

Effect of SiC on the anti-ablation resistance and flexural strength of (Hf-Ta-Zr)C-C/C composites

Ablation behavior and mechanisms of Cf/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C–SiC high-entropy ceramic matrix composites

A novel strategy for rapid fabrication of continuous carbon fiber reinforced (TiZrHfNbTa)C high-entropy ceramic composites: High-entropy alloy in-situ reactive melt infiltration

Fabrication of C/SiC composites by siliconizing carbon fiber reinforced nanoporous carbon matrix preforms and their properties

From Ferroconcrete to Cf/UHTC-SiC: A Totally Novel Densification Method and Mechanism at 1300 °C Without Pressure

Reactive sintering of 2.5D Cf/ZrC-SiC ceramic matrix composite

Novel Synthesis of (hf 0.25 Zr 0.25 Ti 0.25 Ta 0.25 )C-Sic Biphasic Ceramic Micro-Powders Using Single-Source-precursor Route

Novel Synthesis of (Hf0.25zr0.25ti0.25ta0.25)c-Sic Biphasic Ceramic Micro-Powders Using Single-Source-precursor Route

Reactive sintered dense carbon fiber reinforced high‐entropy boride composite using high‐entropy silicide as reactant

Single-source-precursor synthesis of dense monolithic SiC/(Ti0.25Zr0.25Hf0.25Ta0.25)C ceramic nanocomposite with excellent high-temperature oxidation resistance

Construction of sandwich-structured C/C-SiC and C/C-SiC-ZrC composites with good mechanical and anti-ablation properties

Self-densification behavior, interfacial bonding and cyclic ablation resistance of HfSi2-ZrSi2 modified SiC/ZrB2-SiC/SiC coating for Cf/SiC composite

Microstructure and Ablation Behavior of C/C-SiC-(ZrxHf1−x)C Composites Prepared by Reactive Melt Infiltration Method

A novel porous carbon synthesized to serve in the preparation of highly dense and high-strength SiC/SiC by reactive melt infiltration

Enhanced mechanical properties and thermal shock resistance of Cf/ZrB2-SiC composite via an efficient slurry injection combined with vibration-assisted vacuum infiltration

Preparation and Properties of C/SiC Composites Reinforced by High Thermal Conductivity Graphite Films

Microstructures and mechanical properties of high-entropy (Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C ceramics with the addition of SiC secondary phase