Abstract:Tensile properties and fracture mechanisms of SiCf/TC17 composites at room temperature and 773 K were studied. The results show that fiber elastic deformation and matrix yielding contributed to the shapes of the stress-strain curves of SiCf/TC17 composites, which were the bilinear appearance at 298 K and the slight curvature at 773 K. Major fracture mechanism of SiCf/TC17 composites at room temperature were as follows: multiple fractures of the interfacial reaction layer, single fiber fracture, matrix brittle fracture etc.. Typical fracture mechanism of SiCf/TC17 composites at elevated temperature were as follows: multiple fiber fracture, matrix plastic fracture, interface debonding etc.. Fiber cumulating damage theory was proved to be suitable for estimation of the fracture strength of this composite. The calculations of local loading sharing model while taking three or more fibers failure into account and global loading sharing model were close to the experimental values of room temperature and elevated temperature respectively. In addition, according to fracture mechanisms and strength prediction, tensile fracture process of SiCf/TC17 composites at room and elevated temperature were explained in detail. At room temperature, multiple fractures of the interfacial reaction layer started at first, and then the weak fiber fractured gradually and randomly. After critical fiber cluster has been formed by nearby broken fibers, the crack extended into the matrix from these fibers. With the increase of load, the fibers and the matrix at the tip of crack gradually destroyed. At the same time, the cracks from other critical fiber clusters were also expanding and connecting to each other. When the crack area has reached the critical level, the remaining fiber and matrix quickly fractured. However, at elevated temperature the matrix yielded firstly, and then multiple fracture randomly of the interfacial reaction layer and the weak fiber occurred sequentially. The crack from broken fiber deflected at interface between fiber and matrix, caused interface debonding. With the increasing of broken fiber number, the micro-cavities of matrix emerged gradually in the stress concentration area. When the total crack area accumulated by the broken fibers and micro-cavities of matrix has reached the critical level, the remaining fiber and matrix quickly fractured.

Mechanical properties of silicon impregnated C/C composite material at elevated temperature

High-temperature tensile behavior of 3D SiC/SiC composites

Tensile Properties of Two-Dimensional Carbon Fiber Reinforced Silicon Carbide Composites at Temperatures Up to 1800 °C in Air

Mechanical properties and microstructure evolution of 3D C f /SiBCN composites at elevated temperatures

Tensile Mechanical Behavior and Failure Mechanism of a Plain-Woven SiCf/SiC Composites at Room and Elevated Temperatures

Experimental Study of High-Temperature Tensile Mechanical Properties of 3D Needled C/C–SiC Composites

Ambient and Elevated Temperature Mechanical Properties of Hot-Pressed Fused Silica Matrix Composite

Analysis of the Fracture Behavior and Mechanism of PIP-C/SiC Composites at High Temperatures

Tensile Properties of Two-Dimensional Carbon Fiber Reinforced Silicon Carbide Composites at Temperatures Up to 2300 °C

Temperature Resistance Properties of Unidirectional Laminated C f/SiC-Al Prepared by PIP and Vacuum Pressure Infiltration

Thermal Expansion Behavior of Carbon Fiber Reinforced Chemical-Vapor-infiltrated Silicon Carbide Composites from Room Temperature to 1400 °C

Tensile Property of SiC_f/TC17 Composite at Room Temperature

Study on Tensile Behavior of Sicf/Tc17 Composites

Mechanical Properties and Interfaces of Cf/SiC Composites

Compressive Behavior of C/SiC Composites over a Wide Range of Strain Rates and Temperatures

Deformability of a SiCw/6061Al composite during high strain rate compression at elevated temperatures

Tensile behavior of the designed SiCf/Ti2AlNb/Ti17 composites

Tensile properties and fracture behavior of nano-sized SiC particles reinforced AZ91D composites at elevated temperature

Influence of High-Temperature Oxidation and Test Conditions on the Dynamic Mechanical Properties of 2.5D SiCf/SiCm Composites

Mechanical properties of polycrystalline Ti3SiC2 at ambient and elevated temperatures

Mechanical Properties of Si3N4/BN Fibrous Monolithic Ceramics at Elevated-Temperature