Abstract:Silicon carbide fiber-reinforced silicon carbide ceramic matrix composites（SiCf/SiC） used in aero-engines are damaged or even failed due to the oxidation and corrosion by high-temperature and high-speed combustion gases. In this work，the gas generation device was used to simulate the complex gas environment in the aircraft engine，and the aviation kerosene mixed with liquid oxygen fuel in a certain proportion was ignited to form a high-temperature and high-speed combustion gas to assess the material. The oxidation test for 10 h and thermal shock test for 1000 cycles in combustion gas environment at 1200 ℃ were conducted on SiCf/SiC composites respectively. And the protective effect of environmental barrier coating（EBC）on SiCf/SiC composites was investigated. Uniaxial tensile tests were conducted on SiCf/SiC composites and SiCf/SiC-EBC composites after combustion gas environment assessment，and their fracture and cross-section micro-morphologies were observed by scanning electron microscopy. The results show that no significant oxidation of fibers and interphases is found in SiCf/SiC composites and SiCf/SiC-EBC composites after oxidation for 10 h in combustion gas environment，and their uniaxial tensile strength decreases by less than 2%. After 1000 thermal shock cycles in combustion gas environment，multiple micro-cracks are formed and oxidative corrosion of the interfacial layer occurs inside the SiCf/SiC composites，and the uniaxial tensile strength decreases by 41.3%. The EBC coating can effectively protect the SiCf/SiC composites from oxidation and corrosion of high-temperature gas，and the uniaxial tensile strength of SiCf/SiC-EBC composites decreases by 16.6% after 1000 thermal shock cycles.

Properties evolution and damage mechanism of SiC/SiC composites after thermal shock at 1300 °C

High-temperature tensile behavior of 3D SiC/SiC composites

Mechanical Properties and Damage Analysis of SiCf/SiC and SiCf/SiC-EBC Composites in High-Temperature Combustion Gas Environment

Influence of Reinforcement with Multimodal Distribution on Thermophysical Properties and Fracture Behavior in Al-Si/SiC Composites Infiltrated under Super-Gravity Field

Thermal Shock and Residual Strength Testing of SiC/SiC Composite Braided Tubes

In-Situ formation of the BSG bubbles toward SiC/SiC composites protection mechanisms under thermal shock treatment

Tensile Mechanical Behavior and Failure Mechanism of a Plain-Woven SiCf/SiC Composites at Room and Elevated Temperatures

Tensile Properties of Two-Dimensional Carbon Fiber Reinforced Silicon Carbide Composites at Temperatures Up to 1800 °C in Air

Thermal Shock Damage and Failure Mechanism of 2D Laminated SiC/SiC with Barium‐Strontium Aluminosilicate‐Based Environmental Barrier Coating

Cyclic Thermal Shock Damage Behavior in CVI SiC/SiC High-Pressure Turbine Twin Guide Vanes

Failure behavior of SiC/SiC with BSAS-based EBC in gas combustion environment

Behavior of Two-Dimensional C/SiC Composites Subjected to Thermal Cycling in Controlled Environments

High temperature bending properties and failure mechanism of 3D needled C/SiC composites up to 2000 °C

Oxidation Behavior of SiC/SiC Composites in Air at High Temperature

High-Temperature Fatigue Degradation Behaviors of a 3D Braided C/SiC with a Thin Interlayer in Different Dry Oxygen Atmospheres

Long-term oxidation resistant SiC/SiC-SiHfBCN composites: A promising thermo-structural material aims for hypersonic roundtrip

Mechanical and thermal shock properties of C f /SiBCN composite: Effect of sintering densification and fiber coating

Microstructure, mechanical properties and thermal shock behavior of h-BN-SiC ceramic composites prepared by spark plasma sintering

Cyclic thermal shock behaviors of carbon fibers reinforced SiCN ceramics with bio-inspired Bouligand-like architectures

Mechanical properties and microstructure evolution of KD‐SA SiCf/BN/SiC CMCs oxidized at different temperatures