Abstract:Fiber-reinforced polymer (FRP) composites modified with ceramic fillers have excellent thermal stability at high temperatures and are applied in aeronautical and aerospace fields. The effect of strain rate on their mechanical behavior at different temperatures (corresponding to different states of FRP composites) is of interest. In this study, dynamic and quasi-static compressive tests of a kind of ceramifiable polymer composites, B 4 C-talc modified high-silica/boron-phenolic (B 4 C-talc_HS/BPh) composites, were examined at 25–1000 °C. A high-temperature split Hopkinson pressure bar with a double-synchronous assembled system was employed to carry out dynamic tests. During the tests, high-speed camera was employed to monitor the progressive failure process, and the failure morphology was examined using an optical microscope. The tests show that the compressive strength decreases with increasing temperature to 600 °C at both low and high strain rates. However, it is found for the first time that the compressive strength increases obviously at 800–1000 °C due to the ceramifiable transition at a high strain rate. Moreover, the influence of temperature and loading rate on the compressive failure behavior of B 4 C-talc_HS/BPh composites was systematically investigated. Shear force dominated the failure under dynamic load at 25–1000 °C, while it was 25–450 °C under quasi-static load. Piece-wise models are developed to describe the temperature and strain-rate dependent evolution behavior of the compressive strength. This research provides basic experimental data on the mechanical properties of B 4 C-talc_HS/BPh composites, which can inform the design, evaluation of integrity, and reliability of thermal protection structures.

Flexural Properties of Carbon-Carbon Composites at Temperatures Up to 2600 °C

Tensile Properties of Two-Dimensional Carbon Fiber Reinforced Silicon Carbide Composites at Temperatures Up to 2300 °C

Influence of Zrc Content on the Elevated Temperature Tensile Properties of Zrcp/W Composites

Tensile Properties of Two-Dimensional Carbon Fiber Reinforced Silicon Carbide Composites at Temperatures Up to 1800 °C in Air

Experimental Study of High-Temperature Tensile Mechanical Properties of 3D Needled C/C–SiC Composites

High temperature bending properties and failure mechanism of 3D needled C/SiC composites up to 2000 °C

Mechanical Properties and Microstructures of Steel-basalt Hybrid Fibers Reinforced Cement-based Composites Exposed to High Temperatures

Compressive experimental method and properties of C/C composites under ultra-high temperature environment

Uniaxial Tensile Behavior, Flexural Properties, Empirical Calculation and Microstructure of Multi-Scale Fiber Reinforced Cement-Based Material at Elevated Temperature

Mechanical Behavior of carbon felt-carbon composites under ultra-high temperature

High-temperature tensile behavior of 3D SiC/SiC composites

Mechanical properties and microstructure evolution of 3D C f /SiBCN composites at elevated temperatures

High-temperature Flexural Mechanical Properties of SiC/SiC Composites

High‐temperature tensile strength and fracture behavior of ZrB2‐SiC‐graphite composite

Thermal Expansion Behavior of Carbon Fiber Reinforced Chemical-Vapor-infiltrated Silicon Carbide Composites from Room Temperature to 1400 °C

Evolution of strain-rate dependent compressive failure behavior of ceramifiable FRP composites at high temperature conditions

Mechanical Property of M40J F /5a06al Composite at Elevated Temperatures

Experimental Description of Thermomechanical Properties of Carbon Fiber-Reinforced Tic Matrix Composites

The three-point bending responses of carbon fiber composite sandwich beams with Y-frame cores at high and low temperatures

Compressive and flexural behavior of carbon fiber-reinforced PPS composites at elevated temperature

Investigation of Flexural Strength of Vycor Glass/Silicone Composites under High Temperature