Abstract:The mechanical properties of cementitious composites before and after exposure to high temperature are affected by calcium–silicate–hydrate (C–S–H) gels. To evaluate the effects of high temperature, plyvinyl alcohol (PVA) fiber content, and the cooling method on properties of cementitious composites, physical, mechanical, and microscopic tests were performed in this study. The target temperatures were 25, 100, 200, 300, 400, 600, and 800 °C. The PVA fiber contents were 0.0, 0.3, 0.6, 0.9, 1.2, and 1.5 vol%. The high-temperature resistance of PVA fiber-reinforced cementitious composite (PVA-FRCC) specimens was investigated through changes in their appearance, mass loss, compressive strength, splitting tensile strength, flexural strength, and microstructure. The results showed that PVA fibers reduced the probability of explosion spalling in the PVA-FRCC specimens exposed to high temperatures. The mass loss rate of samples exposed to temperatures below 200 °C was small and lower than 5%, whereas a significant mass loss was observed at 200 °C to 800 °C. A small rise in the cubic compressive and splitting tensile strengths of samples was found at 400 °C and 300 °C, respectively. Below 400 °C, the fibers were beneficial to the mechanical strength of the PVA-FRCC specimens. Nevertheless, when the temperature was heated above 400 °C, melted fibers created many pores and channels, which caused a decrease in the strength of the specimens. The method of cooling with water could aggravate the damage to the cementitious composites exposed to temperatures above 200 °C. High temperature could lead to the decomposition of the C–S–H gels of the PVA-FRCC samples, which makes C–S–H gels lose their bonding ability. From the perspective of the microstructure, the structure of PVA-FRCC samples exposed to 600 °C and 800 °C became loose and the number of microcracks increased, which confirmed the reduction in macro-mechanical properties.

Thermal and Mechanical Properties of Ultrahigh Toughness Cementitious Composite with Hybrid PVA and Steel Fibers at Elevated Temperatures

Microstructure and Mechanical Properties of High-Toughness Fiber-Reinforced Cementitious Composites after Exposure to Elevated Temperatures

Mechanical Properties and Microstructures of Steel-basalt Hybrid Fibers Reinforced Cement-based Composites Exposed to High Temperatures

EXPERIMENTAL RESEARCH ON IMPACT BEHAVIOR OF CONCRETE-FILLED STEEL TUBE AT ELEVATED TEMPERATURES

Mechanical properties of polyvinyl alcohol-basalt hybrid fiber engineered cementitious composites with impact of elevated temperatures

Blast resistance of hybrid steel and polypropylene fibre reinforced ultra-high performance concrete after exposure to elevated temperatures

Research on mechanical properties of ultra-high performance fiber reinforced cement-based composite after elevated temperature

Uniaxial Tensile Behavior, Flexural Properties, Empirical Calculation and Microstructure of Multi-Scale Fiber Reinforced Cement-Based Material at Elevated Temperature

Study of Ultra-High Performance Concrete Mechanical Behavior under High Temperatures

Thermal resistance of high strength PVA fiber reinforced engineered cementitious composites containing basalt fiber

Insight into the Mechanical Performance of the UHPC Repaired Cementitious Composite System after Exposure to High Temperatures

Flexural Behavior of Ultra-High-Performance Fiber-Reinforced Concrete Beams after Exposure to High Temperatures

Correlation Between Macroscopic Properties and Microscopic Pore Structure in Steel-Basalt Hybrid Fibers Reinforced Cementitious Composites Subjected to Elevated Temperatures

The Effects of High Temperature on Flexural Strengths of High Performance Nano-Modified Cementitious Composites

Mechanical Properties of Polyvinyl Alcohol Fiber-Reinforced Cementitious Composites after High-Temperature Exposure

Mechanical properties of PVA fiber reinforced cementitious composites (PVA-FRCC) after high temperature

Effects of High Temperature and Substitution Rates of Fly Ash on the Mechanical Properties and Microstructures of Steel-Basalt Hybrid Fibers Reinforced Cementitious Composites

Multiscale Prediction of Thermal Damage for Hybrid Fibers Reinforced Cementitious Composites Blended with Fly Ash at High Temperatures

Study on Shear Behavior of Concrete-polymer Cement Mortar at Elevated Temperature

High Temperature Flexural Deformation Properties of Engineered Cementitious Composites (ECC) with Hybrid Fiber Reinforcement

Microstructure and mechanical behaviour of 3D printed ultra-high performance concrete after elevated temperatures