Abstract:High-strength concrete (HSC) has a high compressive strength, high density, excellent durability, and seepage resistance, but its deformation ability is weak. Adding fibers can improve the physical and mechanical properties of HSC. Additionally, the HSC structure may face the threat of fire. In the process of fire extinguishing, the damage mechanism of high-temperature-resistant concrete is complicated due to the different contact conditions with water at different locations. Hence, it is essential to conduct pertinent research on the behavior of fiber-reinforced HSC with different cooling methods after high-temperature action. In this paper, polyvinyl alcohol fiber (PVA fiber) was selected to be added into the HSC to carry out high-temperature experimental research, so as to explore the apparent changes, failure pattern, and mass loss rate of the fiber-reinforced HSC using different cooling methods and analyze the influence of its residual compressive strength and flexural strength. The test results suggest that, with the increase in heating temperature, the color of the specimen's surface transitions from dark blue-gray to white, and the quantity of surface cracks on the specimen gradually rises. The mechanical strength gradually decreases as the heating temperature increases. At a consistent heating temperature, the mechanical strength initially rises, and then falls with an increase in fiber content. The maximum compressive strength and flexural strength were achieved at PVA fiber contents of 0.2% and 0.3%, respectively. For different temperatures and fiber contents, the mechanical strength after natural cooling is generally higher than that after immersion cooling. In addition, X-ray polycrystalline diffractometry (XRD) and scanning electron microscopy (SEM) tests were conducted to analyze the compositional alterations and microstructure of the fiber-reinforced HSC following high-temperature exposure, accompanied by an explanation of the factors influencing the alterations in the physical and mechanical properties. Therefore, the findings of this study can serve as a valuable reference for the utilization of HSC in engineering structures and contribute to the advancement of HSC technology.

The Effects of High Temperature on Flexural Strengths of High Performance Nano-Modified Cementitious Composites

EFFECT OF HIGH TEMPERATURE ON NANO-MODIFIED CEMENTITIOUS COMPOSITES

Microstructure and Mechanical Properties of High-Toughness Fiber-Reinforced Cementitious Composites after Exposure to Elevated Temperatures

Mechanical Properties of Polyvinyl Alcohol Fiber-Reinforced Cementitious Composites after High-Temperature Exposure

Mechanical properties of PVA fiber reinforced cementitious composites (PVA-FRCC) after high temperature

Mechanical Properties and Microstructures of Steel-basalt Hybrid Fibers Reinforced Cement-based Composites Exposed to High Temperatures

Thermal and Mechanical Properties of Ultrahigh Toughness Cementitious Composite with Hybrid PVA and Steel Fibers at Elevated Temperatures

Effects of High Temperature and Substitution Rates of Fly Ash on the Mechanical Properties and Microstructures of Steel-Basalt Hybrid Fibers Reinforced Cementitious Composites

Uniaxial Tensile Behavior, Flexural Properties, Empirical Calculation and Microstructure of Multi-Scale Fiber Reinforced Cement-Based Material at Elevated Temperature

Correlation Between Macroscopic Properties and Microscopic Pore Structure in Steel-Basalt Hybrid Fibers Reinforced Cementitious Composites Subjected to Elevated Temperatures

Mechanical properties of polyvinyl alcohol-basalt hybrid fiber engineered cementitious composites with impact of elevated temperatures

High Temperature Flexural Deformation Properties of Engineered Cementitious Composites (ECC) with Hybrid Fiber Reinforcement

Effect of fibers addition on mechanical properties of eco-friendly phosphogypsum-based composite at high temperatures

Study of Ultra-High Performance Concrete Mechanical Behavior under High Temperatures

Effect of Fibers on High-Temperature Mechanical Behavior and Microstructure of Reactive Powder Concrete

An Experimental Study on the Influence of Different Cooling Methods on the Mechanical Properties of PVA Fiber-Reinforced High-Strength Concrete after High-Temperature Action

Research on mechanical properties of ultra-high performance fiber reinforced cement-based composite after elevated temperature

A review of high temperature properties of cement based composites: Effects of nano materials

Thermal resistance of high strength PVA fiber reinforced engineered cementitious composites containing basalt fiber

Effect of Cooling Method on Physical and Mechanical Properties of PVA Fiber-Reinforced High-Strength Concrete Exposed to High Temperature

MECHANICAL PROPERTY OF FINE GRAINED CONCRETE WITH DIFFERENT CEMENTING MATERIAL AFTER EXPOSURE TO HIGH-TEMPERATURE