Abstract:The near stoichiometric SiC fiber has been reported to play significant roles in the application of aero‐engine field. An in‐depth understanding on the degradation mechanism of the fiber during its corrosion in air and under a simulated aeroengine environment (PH2O: PO2: PAr = 14:8:78 kPa) will shine a light on the performance evaluations of the near stoichiometric SiC fiber‐based materials as well as the development of their potential applications. In this study, .XRD, SEM, and FIB‐TEM were utilized to analyze the mechanical properties and microstructure of the fiber. After oxidation in dry air and Ar‐H2O‐O2 for 1h, respectively the fiber strength retention rate has been found to decreases with the increased oxidation temperature. The raise in oxidation temperature also led to the increasing of the thickness and the crystallization rate of the oxide scale. The most different oxidation behavior of SiC being treated under the simulated environment than in air is the lower oxidation activation energy and the higher crystallization activation energy for cristobalite. Water vapor can promote the oxidation reaction and inhibit the crystallization of cristobalite in the oxide scale. Few significant differences have been observed otherwise in the oxidation process and oxidation chromatography crystallization mechanism of fibers being treated under different conditions.. The increase of oxide layer thickness and the formation of cristobalite impair the structural integrity and compactness of the oxide scale and thus leads to the deterioration of the mechanical properties of SiC fibers. Therefore, it is proposed that oxidation resistance of SiC fiber can be improved by insulating the reaction between the oxidizing agents and the SiC fiber, or by increasing the crystallization temperature of cristobalite in the oxidation process and reducing the crystallization rate. This article is protected by copyright. All rights reserved

Preparation and high-temperature properties of skin–core structure SiC ceramic fibers

Effect of long-time annealing at high temperature on the microstructure and mechanical properties of different types of SiC fibers

The fiber structure evolution and performance changes of SiC–ZrC fibers after 1600 °C heat treatment

Flexible ultrafine nearly stoichiometric polycrystalline SiC fibers with excellent oxidation resistance and superior thermal stability up to 1900 °C

Long-time oxidation behavior of the nearly stoichiometric polycrystalline SiC fibers under air atmosphere at different temperatures

Preparation of silicon-nitride ceramic fibers with hafnium compounds loaded on the surface and the high temperature properties

Oxidation and mechanical properties of SiC fibers after high temperature exposure in air and steam

SiC fibers with different diameters exhibiting excellent high-temperature resistance and oxidation resistance

High-temperature resistance and thermal insulation performance of continuous SiMOC ceramic fibers fabricated by the modified sol-gel method combined with dry spinning

Fabrication of SiC ultrafine fiber with low oxygen content by electrospinning, thermal curing and pyrolysis of cyano-polycarbosilane

Mechanical properties and microstructural evolution of Cansas-III SiC fibers after thermal exposure in different atmospheres

Characterization and high-temperature degradation mechanism of continuous silicon nitride fibers

Multi-phase SiZrOC nanofibers with outstanding flexibility and stability for thermal insulation up to 1400 °C

High-Temperature Fatigue Degradation Behaviors of a 3D Braided C/SiC with a Thin Interlayer in Different Dry Oxygen Atmospheres

Mechanical properties and microstructure evolution of KD‐SA SiCf/BN/SiC CMCs oxidized at different temperatures

Microstructure and corrosion behavior of in-situ grown Y3Si2C2 coated SiC fibers exposed to air and wet-oxygen at 1400 °C

Structural evolution and mechanical properties of Cansas-III SiC fibers after thermal treatment up to 1700 °C

Oxidation of SiC fibers in water vapor

Boron-carbon doped Silicon Carbide Fibers: Preparation and Property

Degradation mechanism of near stoichiometric SiC fibers after air and Ar‐H2O‐O2 corrosion at 1000∼1500°C

Study of online tensile properties for continuous ceramic fibers under high‐temperature loads