Abstract:The near stoichiometric SiC fiber has been reported to play significant roles in the application of aero‐engine field. An in‐depth understanding on the degradation mechanism of the fiber during its corrosion in air and under a simulated aeroengine environment (PH2O: PO2: PAr = 14:8:78 kPa) will shine a light on the performance evaluations of the near stoichiometric SiC fiber‐based materials as well as the development of their potential applications. In this study, .XRD, SEM, and FIB‐TEM were utilized to analyze the mechanical properties and microstructure of the fiber. After oxidation in dry air and Ar‐H2O‐O2 for 1h, respectively the fiber strength retention rate has been found to decreases with the increased oxidation temperature. The raise in oxidation temperature also led to the increasing of the thickness and the crystallization rate of the oxide scale. The most different oxidation behavior of SiC being treated under the simulated environment than in air is the lower oxidation activation energy and the higher crystallization activation energy for cristobalite. Water vapor can promote the oxidation reaction and inhibit the crystallization of cristobalite in the oxide scale. Few significant differences have been observed otherwise in the oxidation process and oxidation chromatography crystallization mechanism of fibers being treated under different conditions.. The increase of oxide layer thickness and the formation of cristobalite impair the structural integrity and compactness of the oxide scale and thus leads to the deterioration of the mechanical properties of SiC fibers. Therefore, it is proposed that oxidation resistance of SiC fiber can be improved by insulating the reaction between the oxidizing agents and the SiC fiber, or by increasing the crystallization temperature of cristobalite in the oxidation process and reducing the crystallization rate. This article is protected by copyright. All rights reserved

Microstructure and corrosion behavior of in-situ grown Y3Si2C2 coated SiC fibers exposed to air and wet-oxygen at 1400 °C

Microstructure and Wet-Oxygen Corrosion Behaviors of In-Suit Grown Y3Si2C2 Modified SiCf/SiC Composites

In-situ Grown Y3Si2C2 on RB-SiC Ceramic for Enhanced Wet-Oxygen Corrosion Resistance

Oxidation Behavior of SiCf/SiC Composites Modified by Layered-Y2Si2O7 in Wet Oxygen Environment

Enhanced wet-oxidation resistance of Y2O3 modified SiC ceramics by the formation of Y2Si2O7 protective layer

Long-time oxidation behavior of the nearly stoichiometric polycrystalline SiC fibers under air atmosphere at different temperatures

Degradation mechanism of near stoichiometric SiC fibers after air and Ar‐H2O‐O2 corrosion at 1000∼1500°C

The Oxidation Behavior and Corrosion Mechanism of SiC Matrix Ceramics in a High Temperature Wet Air Environment

Mechanical properties and microstructural evolution of Cansas-III SiC fibers after thermal exposure in different atmospheres

The Comparative Investigation of Oxidation Behavior and Corrosion Mechanisms of SiC Matrix Ceramics under Different Atmospheres

Fabrication and oxidation resistance of mullite/yttrium silicate multilayer coatings on C/SiC composites

The fiber structure evolution and performance changes of SiC–ZrC fibers after 1600 °C heat treatment

Oxidation of Short Carbon Fiber Reinforced Zrb2-Sic Ceramics under Atmospheric and Oxyacetylene Torch Conditions

Mechanical properties and microstructure evolution of KD‐SA SiCf/BN/SiC CMCs oxidized at different temperatures

Oxidation of SiC fibers in water vapor

Thermal shock behavior and oxidation resistance of novel SiC nanowires+Si/Yb2Si2O7-Si/Yb2Si2O7 environmental barrier coatings

Thermal cycling behavior of bi-layer Yb2Si2O7/SiC EBC-coated Cf/SiC composites in burner rig tests

Preparation and high-temperature properties of skin–core structure SiC ceramic fibers

Oxidation and mechanical properties of SiC fibers after high temperature exposure in air and steam

Oxidation behavior of SiC‐AlN ceramics exposed to dry oxygen and water oxygen environments at 1100–1300°C

Microstructure And Oxidation Resistance Of Carbon/Carbon Composites Coated With Si3n4-Si/Mosi2-Sic Multi-Layers By Slurry Coating And Post Heat-Treatment Process