Abstract:An unidirectional ultra-high modulus M40J carbon fiber reinforced 5A06 aluminum alloy with volume fraction of 55% was fabricated by the pressure infiltration method. The effect of thermal cycling (−70 to 120°C and −196 to 120°C) on the mechanical properties of Cf/Al composites was investigated. Bending modulus increased abruptly after five thermal cycles and then reached a platform. However, after 50 cycles, the bending modulus decreased with the increase of cycles due to generation and propagation of microcracks at C fiber/Al interface. The bending strength of composites showed fluctuations between 800 and 1000MPa, and the amount and length of pull-out fiber increased with the increase of the thermal cycling times regardless of temperature difference. Microstructure observation revealed the formation of microcracks and interface debonding at the C fiber/Al interface after thermal cycling treatment, and the amount of the microcracks and interface debonding increased with the temperature difference. The main interfacial products in annealed Cf/Al composites were rod-like Al3Mg2 and bulky Al58Mg42, and no significant Al4C3 was observed at C fiber/Al interface. The thermal cycling treatment used in the present work had little effect on the interface microstructure of Cf/Al composites. Very few dislocations were observed in the Al matrix of annealed Cf/Al composites. However, the amount of dislocations in the Al matrix increased gradually with the increase of thermal cycles. Moreover, the amount of dislocations would decrease after a certain thermal cycles due to movement and annihilation of unlike-sign dislocations.

Effect of high temperature annealing on microstructure and mechanical properties of Morlion735 alumina fiber

Effect of Annealing on the Microstructure and Magnetic Properties of Fe-based Nanocomposite Materials

Effect of thermal exposure on the microstructure and strength of an alumina‐silica ceramic fiber

Microstructure evolution and mechanical behavior of a mullite fiber heat‐treated from 1100 to 1300°C

Effect of heat‐treatment on the microstructure and room‐temperature mechanical properties of alumina–silica fiber

Strength degradation of alumina fiber: Irreversible phase transition after high-temperature treatment

Effect of annealing on tensile and thermal expansion properties of Mg2B2O5 whisker-reinforced aluminum composite

Effects of sintering temperature on mechanical properties of alumina fiber reinforced alumina matrix composites

Preparation and mechanical performance of ductile Csf/Al2O3-BN composites, Part 1: Effects of fiber length and sintering temperature

Mechanical Property of M40J F /5a06al Composite at Elevated Temperatures

Effect of annealing temperature on microstructure and tensile properties of copper/aluminum composite thin strip

Effect of thermal exposure on interface and tensile properties of aluminum borate whisker reinforced pure aluminum composite

Effects Of High-Temperature Annealing On Structural And Optical Properties Of Highly Ordered Porous Alumina Membranes

Effect of Sintering Temperature on Microstructure and Mechanical Behavior of Alumina-Based Ceramic Shell by SLS

Effect of thermal cycling on the mechanical properties of Cf/Al composites

The Effect of Annealing Temperature on Micro-Structure and Mechanical Properties of C/Sic Composites

Effect of annealing on microstructure and mechanical properties of an Al–Mg-Sc-Zr alloy

Effect of long-time annealing at high temperature on the microstructure and mechanical properties of different types of SiC fibers

Effect of Annealing on Anisotropic Tensile Properties of Al–12%Si Alloy Fabricated by Laser Powder Bed Fusion

Effect of hafnium oxide on continuous aluminum oxide-mullite-hafnium oxide composite ceramic fibers

Effect of annealing process on microstructure and mechanical properties of precipitated phase of A1235 aluminum alloy