Abstract:The influence of water content on the crystallization of the microporous aluminophosphate AlPO4-11 was investigated by a combination of in situ UV Raman and ex situ XRD and NMR characterizations. Under high water content conditions (Al2O3:H2O=1:20–69), an AlPO4-5 intermediated formed first and later co-existed with AlPO4-11. In the last stage of crystallization, the crystalline AlPO4-5 completely disappeared and well-crystallized AlPO4-11 was obtained. The position of the three signals observed in the 31P MAS NMR spectra of the isolated solid samples did not change during the hydrothermal treatment, suggesting that the fragments containing the P site in the junction of 6- and 4-membered rings of both AlPO4-5 and AlPO4-11 formed first and that the environments of the P sites were very similar to those in the final structure. A significant increase of Al concentration in liquid media was observed before the appearance of XRD detectable AlPO4-11. Under low water content conditions (Al2O3:H2O=1:15), the AlPO4-11 was directly crystallized from the initial mixture. In situ Raman spectra showed that the 10-membered rings were complete by the time the transformation of octahedral Al to tetrahedral Al was finished and that the conformation of the protonated di-(i-propyl)amine changed little during the crystallization. The present study showed that the composition of the liquid phase is critical to the formation of a specific structure.

Synthesis and crystal morphology control of AlPO4-5 molecular sieves by microwave irradiation

Microwave preparation of molecular sieve AlPO4-5 with nanometer sizes

Multinuclear solid-state NMR studies on the formation mechanism of aluminophosphate molecular sieves in ionic liquids

Studies on preparing molecular sieves AIPO4-5 and AIPO4-11 by the vapour phase method

Synthesis of the Molecular-Sieve Alpo4-5 with an Unequal Molar Ratio of Al2o3 to P2o5

Cooperative structure-directing effect in the synthesis of aluminophosphate molecular sieves in ionic liquids.

Ionothermal Synthesis Process for Aluminophosphate Molecular Sieves in the Mixed Water/ionic Liquid System

Ionothermal Synthesis of Hierarchical Structured CuAPO-5 Molecular Sieve

Molecular engineering of microporous crystals: (III) The influence of water content on the crystallization of microporous aluminophosphate AlPO4-11

Synthesis of Single Crystals of Aluminosphate-Based Molecular Sieves

New Insights into the Role of Amines in the Synthesis of Molecular Sieves in Ionic Liquids.

Synthesis of Aluminophosphate Molecular Sieves in Alkaline Media

Stability and characterization of mesoporous molecular sieve using natural clay as a raw material obtained by microwave irradiation

Vapor Phase Transport Synthesis and Structure Characterization of an Aluminophosphate Molecular Sieve [Al3P3O12F][C5H5NH]center dot 0.2H(2)O

Effect of Solubility of Aluminum Sources and Iron Loadings on the Structure and Morphology of FeAIPO-5 Molecular Sieves

Ultrafast synthesis of discrete submicron AlPO4-LTA molecular sieve crystals and their application in molecular sieve membrane

SYNTHESIS AND CHARACTERIZATION OF SILICOALUMINOPHOSPHATE MOLECULAR SIEVES FROM METAKAOLIN

Template control in ionothermal synthesis of aluminophosphate microporous materials.

Insights of the Crystallization Process of Molecular Sieve AlPO4-5 Prepared by Solvent-Free Synthesis.

Synthesis and characterization of a new mesoporous molecular sieve

Synthesis and Characterization of Aluminophosphate Molecular Sieve AlPO4-41 from Alcohol Systems