Abstract:TiO2 nanocrystallines with a size of 3–7 nm have been synthesized by the sol–gel method with excessive water at a low temperature of about 50°C. The effects of amount of water and pH on the formation of sols and powders containing TiO2 nanocrystallines were investigated by X‐ray powder diffraction (XRD), transmission electron microscopy, and high‐resolution transmission electron microscopy. The results showed that a pure anatase phase was formed at pH 1, in contrast to the formation of particles with a mixture of anatase and brookite phases at pH 2–7. Moreover, at pH 1, the intensity of the XRD peaks and the crystal size increased with increasing water content when the water ratio increased from 40 to 100. Whereas the crystal intensity remained invariant, the crystal size still increased when the water ratio increased from 100 to 400. The photocatalytic activity was also investigated. It was shown that when the water ratio was below 100, the photocatalytic activity increased with increasing water content. Further increase of the water content decreased the photocatalytic activity. The photocatalytic activity decreased with increasing pH. All samples with pH=1 showed better photocatalytic activity than Degussa P25. Mechanisms for the formation of the TiO2 nanocrystalline particles at such a low temperature were also discussed.

Effect of Precursor pH on One-dimensional Growth of Mullite Prepared by Sol-Gel Method with WO_3 Catalyst

Effect of precursor pH on one-dimensional growth of mullite prepared by sol-gel method with WO<SUB>3</SUB> catalyst: Effect of precursor pH on one-dimensional growth of mullite prepared by sol-gel method with WO<SUB>3</SUB> catalyst

Synthesis and Controlled Growth of Mullite Submicron Powders

Effect of Magnesium Oxide on Preparation of Mullite Fibers Via Sol-Gel Method

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature

Effect of Ph in Preparation and Properties of Mesoporous Sieve from Montmorillonite

Morphology-controlled Synthesis and Characterization of MnWO4 Nanocrystals Via a Facile, Additive-Free Hydrothermal Process

pH control on preparation of nano-TiO_2 by gel-sol process

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Hydrothermal Preparation and Characterization of MnWO4Nanowires

Effect of the alumina and silica source mixing procedure on the microstructural evolution of alumina-mullite composite fibers prepared by sol–gel method

Structural Studies of Wo3-Catalysed Mullite

Preparation of Nanometer Mullite Via Supercritical CO2

Fabrication and characterization of porous mullite ceramics with ultra-low shrinkage and high porosity via sol-gel and solid state reaction methods

Mullite Fibers Prepared from an Inorganic Sol–gel Precursor

Preparation of Mullite Monoliths with Well-Defined Macropores and Mesostructured Skeletons Via the Sol–gel Process Accompanied by Phase Separation

The Effect of Al Content on the Pore Diameters of the Mesoporous Molecular Sieves Synthesized with Microcline as Starting Material

Preparation of Nanometer Mullite via Supercritical CO<sub>2</sub>

Effect of the Way of Water Addition on the Morphology of Nano-Sized Al2O3 Powders Prepared by Sol-Gel Method

Effect of pH and sulphate on the morphology of γ-AlOOH

Preparation and Mechanism of Nano Mullite Powders from Kaolin Via Open Hydrothermal Process.