Abstract:The preparation of precursor sol is the first and crucial step in fabricating oxide fibers by the sol–gel method. In this study, different aluminum-silica sols were prepared by adjusting the alumina and silica source mixing procedure using aluminum carboxylate sol and tetraethoxysilane (TEOS) as the aluminum source and silicon source, respectively. Continuous alumina-mullite precursor fibers were obtained by dry spinning and the effects of alumina and silica source mixing procedure on the phase transition and microstructure evolution of alumina-mullite composite fibers were investigated. The results showed that the mullite formation temperature in the fibers obtained by adding TEOS during the preparation of aluminum carboxylate sol was about 1300 °C, while it was 800 °C in the fibers obtained by mixing aluminum carboxylate sol and TEOS. In addition, the grain size of the fibers obtained by adding TEOS during the preparation of aluminum carboxylate sol was significantly smaller than that obtained by mixing aluminum carboxylate sol and TEOS. The mechanism of this difference was that the aluminum-silica sol obtained by adding TEOS during the preparation of aluminum carboxylate sol was a diphasic sol, while the aluminum-silica sol obtained by adding TEOS in the prepared aluminum carboxylate sol was a monophasic sol.Graphical Abstract

Fabrication of ultrafine mullite powders

Fabrication of Fine Mullite Powders by Heterogeneous Nucleation and Growth Processing

Fabrication of Mullite Powders by A Novel Processing

Fabrication of Composite Coating Particles with Mullite Stoichiometric Ratio by a Novel Processing

The Effects of Mineral Composition and Sintering Temperature on Synthetic Mullite

Fabrication of Α-Alo(oh)·sio2 with Core-Shell Structures by Heterogeneous Nucleation-and-growth Processing

Preparation of composite coating particles of α-Al2O3–SiO2 by heterogeneous nucleation-and-growth processing

Fabrication and Properties of Porous Mullite Ceramics from Directly Sintering Ceramic Microspheres

Fabrication and Characterization of Porous Mullite Coating on Porous Silicon Carbide Support

Preparation of Core/Shell Structure of α-Al(OH) 3 -SiO 2 by Heterogeneous Nucleation-and-Growth Processing

PREPARATION OF NANO-SiO2-COATED Al2O3 CONCENTRATED SUSPENSION AND ITS GEL CASTING

Porous mullite nanopowder for slurry preparation of material direct writing by sol-gel method

Preparation and properties of porous mullite-based ceramics fabricated by solid state reaction

Fabrication of composite particles with core-shell structures by a novel processing

Preparation of Dense Mullite Ceramics through Gelcasting of Alumina Slurry Dispersed in Silica Sol

Synthesis and Controlled Growth of Mullite Submicron Powders

Effect of the alumina and silica source mixing procedure on the microstructural evolution of alumina-mullite composite fibers prepared by sol–gel method

Preparation of Nanocrystalline Mullite Contained Microspheres by Sol-gel Process in Oil-in-Water Emulsion

Preparation and research of fine-grained alumina with high mechanical properties

A simple and efficient hydratable alumina gel‐casting method for the fabrication of high‐porosity mullite ceramics