Abstract:In the present work, a novel microchannel device was developed and used for the preparation of core-shell microspheres combining with a dextran/poly(ethylene glycol) diacrylate (DEX/PEGDA) aqueous two-phase system. Silica@silica core-shell microspheres were prepared as a model material. Silica@silica core-shell microspheres with different sizes of cores and thicknesses of shells were prepared by using different flowrate ratios of DEX/silica and PEGDA/silica aqueous solutions. The content of colloidal silica and the calcination temperature have a significant effect on the texture properties of the prepared core-shell microspheres. The surface area decreased from 199 to 177 m2/g with an increase in the colloidal silica content from 30 to 60 wt %. For a specific colloidal silica content (50 wt %), with the increase in calcination temperature from room temperature to 650 °C, the total pore volume went through a maximum of 0.7 cm3 g-1 with a surface area of 178 m2 g-1 and pore size of 7.32 nm at 450 °C. Due to the accumulation of metal nanoparticles in DEX, different metal nanoparticles (Ni and Pd) were successfully introduced into the core of the core-shell microspheres for the preparation of silica/metal nanoparticles@silica core-shell microsphere catalysts. The catalysts showed similar catalytic performance as the metal nanoparticles for hydrogenation of 4-nitrophenol with a conversion higher than 95%. However, the core-shell microsphere catalyst is much easier to recover. The reuse experiments indicated that the core-shell catalyst has high stability.

Fabrication of composite particles with core-shell structures by a novel processing

Fabrication of Composite Coating Particles with Mullite Stoichiometric Ratio by a Novel Processing

Preparation of Core-Shell Inorganic Nano-Particles

Fabrication of Α-Alo(oh)·sio2 with Core-Shell Structures by Heterogeneous Nucleation-and-growth Processing

Preparation of composite coating particles of α-Al2O3–SiO2 by heterogeneous nucleation-and-growth processing

Preparation of Core/Shell Structure of α-Al(OH) 3 -SiO 2 by Heterogeneous Nucleation-and-Growth Processing

Fabrication of Composite Coating Spheres with Silica Sphere/titania Shell Structure by Heterogeneous Nucleation-and-growth Processing

Preparation of Core-Shell Polycarbonate/BaSO_4 Submicron Composite Particles

Fabrication of Fine Mullite Powders by Heterogeneous Nucleation and Growth Processing

Fabrication of Mullite Powders by A Novel Processing

Study on the densification of composite coating particles of α-Al2O3–SiO2

The Synthesis of a Core–shell Hybrid Composite Micro-Sphere with Controllable Homogenous or Heterogeneous Multi-Shell Structure by Multiple-Growth Via a Combination Method

Fabrication and characterization of silver core and porous silica shell nanocomposite particles

Fabrication of ultrafine mullite powders

Preparation of Bigger Core-Shell PS/PMMA Composite Particles by Suspension-Emulsion Combined Polymerization

Preparation and Characterization of Nio((Core))/Fe2o3((Shell)) Composite Particles

Factors Influencing on the Preparation of Ultrafine Energetic Core-shell Composite Materials

Synthesis and Characterization of ZSM-5/amorphous Silica Composite Materials

Preparation of Silica@Silica Core-Shell Microspheres Using an Aqueous Two-Phase System in a Novel Microchannel Device.

Preparation of metallodielectric composite particles with multishell structure.

Synthesis and Characterization of Silica–silver Core–shell Composite Particles with Uniform Thin Silver Layers