Abstract:To improve the thermal and mechanical properties of Al2O3/AlN composite ceramics, a novel heterogeneous precipitation coating (HPC) approach was introduced into the fabrication of Al2O3/AlN ceramics. For this approach, Al2O3 and AlN powders were coated with a layer of amorphous Y2O3, with the coated Al2O3 and AlN powders found to favor the formation of an interconnected YAG second phase along the grain boundaries. The interconnected YAG phase was designed to act as a diffusion barrier layer to minimize the detrimental interdiffusion between Al2O3 and AlN particles. Compared with samples prepared by a conventional ball-milling method, the HPC Al2O3/AlN composites exhibited less AlON formation, a higher relative density, a smaller grain size and a more homogeneous microstructure. The thermal conductivity, bending strength, fracture toughness and Weibull modulus of the HPC Al2O3/AlN composite ceramics were found to reach 34.21 ± 0.34 W m−1 K−1, 475.61 ± 21.56 MPa, 5.53 ± 0.29 MPa m1/2 and 25.61, respectively, which are much higher than those for the Al2O3 and Al2O3/AlN samples prepared by the conventional ball-milling method. These results suggest that HPC is a more effective technique for preparing Al2O3/AlN composites with enhanced thermal and mechanical properties, and is probably applicable to other composite material systems as well.

Preparation of composite coating particles of α-Al2O3–SiO2 by heterogeneous nucleation-and-growth processing

Preparation of Core/Shell Structure of α-Al(OH) 3 -SiO 2 by Heterogeneous Nucleation-and-Growth Processing

Fabrication of Composite Coating Particles with Mullite Stoichiometric Ratio by a Novel Processing

Fabrication of Α-Alo(oh)·sio2 with Core-Shell Structures by Heterogeneous Nucleation-and-growth Processing

Fabrication of composite particles with core-shell structures by a novel processing

Study on the densification of composite coating particles of α-Al2O3–SiO2

Fabrication of Fine Mullite Powders by Heterogeneous Nucleation and Growth Processing

Fabrication of Composite Coating Spheres with Silica Sphere/titania Shell Structure by Heterogeneous Nucleation-and-growth Processing

Fabrication of ultrafine mullite powders

Fabrication of Mullite Powders by A Novel Processing

Surface Modification Of Nano-Sic Powders By Coating With Heterogeneous Nucleation Process

Synthesis and Characterization of Aluminum Particles Coated with Uniform Silica Shell

Preparation of NiAl2O4/Al2O3 composite nanopowder

Preparation and properties of Al2O3/Al-2(1-0.2)Mg0.2Ti(1+0.2)O5 matrix ceramic composite

Preparation of MgAl2O4-Coated Al2O3np and Migration of Ceramic Nanoparticles during Ultrasonic Processing of Aluminum Matrix Composites

Effect of composite additives on phase transition and dispersibility of α-Al2O3

Preparation and Characterization of Al2O3–TiO2Composite Oxide Nanocrystals

Fabrication of Al2O3/AlN composite ceramics with enhanced performance via a heterogeneous precipitation coating process

The Process Study of SiO2 Coating on α-FeOOH Particles by Surface Hydrolysis Reaction in Fluidized BED Reactor

Rare-Earth Oxide Coating for Sub-Micro Particulates Reinforced Aluminum Matrix Composites

Preparation of Composite Spherical Alumina Nanoparticles and Study on their CMP Performance