Abstract:To improve the thermal and mechanical properties of Al2O3/AlN composite ceramics, a novel heterogeneous precipitation coating (HPC) approach was introduced into the fabrication of Al2O3/AlN ceramics. For this approach, Al2O3 and AlN powders were coated with a layer of amorphous Y2O3, with the coated Al2O3 and AlN powders found to favor the formation of an interconnected YAG second phase along the grain boundaries. The interconnected YAG phase was designed to act as a diffusion barrier layer to minimize the detrimental interdiffusion between Al2O3 and AlN particles. Compared with samples prepared by a conventional ball-milling method, the HPC Al2O3/AlN composites exhibited less AlON formation, a higher relative density, a smaller grain size and a more homogeneous microstructure. The thermal conductivity, bending strength, fracture toughness and Weibull modulus of the HPC Al2O3/AlN composite ceramics were found to reach 34.21 ± 0.34 W m−1 K−1, 475.61 ± 21.56 MPa, 5.53 ± 0.29 MPa m1/2 and 25.61, respectively, which are much higher than those for the Al2O3 and Al2O3/AlN samples prepared by the conventional ball-milling method. These results suggest that HPC is a more effective technique for preparing Al2O3/AlN composites with enhanced thermal and mechanical properties, and is probably applicable to other composite material systems as well.

Fabrication of Mullite Powders by A Novel Processing

Fabrication of Fine Mullite Powders by Heterogeneous Nucleation and Growth Processing

Fabrication of Composite Coating Particles with Mullite Stoichiometric Ratio by a Novel Processing

Fabrication of ultrafine mullite powders

Fabrication of Α-Alo(oh)·sio2 with Core-Shell Structures by Heterogeneous Nucleation-and-growth Processing

Fabrication of Homogeneous Mullite-Based Fiber Porous Ceramics with High Strength and Porosity

The Effects of Mineral Composition and Sintering Temperature on Synthetic Mullite

Fabrication of composite particles with core-shell structures by a novel processing

Fabrication of Composite Coating Spheres with Silica Sphere/titania Shell Structure by Heterogeneous Nucleation-and-growth Processing

Preparation of composite coating particles of α-Al2O3–SiO2 by heterogeneous nucleation-and-growth processing

Preparation of Core/Shell Structure of α-Al(OH) 3 -SiO 2 by Heterogeneous Nucleation-and-Growth Processing

Preparation of Ti/Al based nanophase composite powder by mechanical alloying

Fabrication and Characterization of Porous Mullite Coating on Porous Silicon Carbide Support

Fabrication and Properties of Porous Mullite Ceramics from Directly Sintering Ceramic Microspheres

Preparation of ti-al based nanophase composite powder by mechanical alloying

Preparation of Dense Mullite Ceramics through Gelcasting of Alumina Slurry Dispersed in Silica Sol

A novel aqueous gel-casting for fabricating Al2O3-bonded fibrous mullite ceramics

Fabrication of Al2O3/AlN composite ceramics with enhanced performance via a heterogeneous precipitation coating process

Preparation and properties of porous mullite-based ceramics fabricated by solid state reaction

Synthesis of mullite ceramics from powdered mine tailings reinforced with Al2O3