Abstract:The possibility of reusing ceramic roller waste to produce cordierite and mullite refractories was investigated. Five batches were designed using wastes representing ceramic roller waste, magnesite, and silica sand, shaped and fired at 1300 °C/2 h, and one batch was selected at 1200 °C. The chemical composition and precipitated phases of the used raw materials and the fired batches were analyzed using XRF and XRD techniques, respectively. Densification parameters, morphology, microstructure and electrical properties were also studied to evaluate the effect of the formed phases on the properties of fired materials. Bulk density increases with an increase in mullite and a decrease in cordierite, and it also increases with increasing temperature, whereas porosity and water absorption show a opposite behavior to density (it decreases with an increase in mullite and temperature). The main phases developed after firing at 1300 °C/2 h were cordierite, mullite, corundum, baddeleyite, and spinel. Bending strength increases with increasing mullite percentage and density, and decreasing grain size and porosity. The microstructure develops and becomes finer with increasing mullite percentage and density. The grain size of the crystals was very fine at 1200 °C/2 h and increased at 1300 °C/2 h. Broadband dielectric spectroscopy was employed to study the electrical and dielectric behavior of the investigated samples. The increase in mullite concentration shows a remarkable increase in ε', especially at lower frequencies, as it is three times higher than that of M10. At f > 103 Hz ε', frequency independence is accompanied by an increase in mullite concentrations due to the lag of dynamics fluctuations after the alteration of the electric field. The generation of new free ions leads to the enhancement of conductivity as the mullite concentration increases.

Synthesis of mullite ceramics from powdered mine tailings reinforced with Al2O3

The Effects of Mineral Composition and Sintering Temperature on Synthetic Mullite

Mining tailings as raw materials for reaction-sintered aluminosilicate ceramics: Effect of mineralogical composition on microstructure and properties

Synthesis of mullite from wasted silica brick, wasted fireclay brick and wasted slide gate

Mullite-Based Ceramics from Mining Waste: A Review

Preparation and properties of Al2O3/Al-2(1-0.2)Mg0.2Ti(1+0.2)O5 matrix ceramic composite

Preparation of low-cost mullite ceramics from natural bauxite and industrial waste fly ash

Industrial waste silica-alumina gel recycling: Low-temperature synthesis of mullite whiskers for mass production

Preparation of mullite ceramics with equiaxial grains from powders synthesized by the sol-gel method

Optimized synthesis of mullite ceramics in thermal plasma

Fabrication of Mullite Powders by A Novel Processing

Reaction-Sintered Porous Mineral-Based Mullite Ceramic Membrane Supports Made From Recycled Materials

Novel process for synthesizing fused mullite from titanium-rich medium/low grade or waste bauxite

Effect Of Y2o3 On Property Of Mullite Ceramic Enhanced By Andalusite

Preparation and Characterization of Mullite Whiskers from Different Silica Sources via Molten Salt Reaction

Sintering mechanism and properties of corundum-mullite duplex ceramic with MnO2 addition

Synthesis and characterization of ceramic refractories based on industrial wastes

Thermal decomposition and reaction sintering for synthesis of mullite-zirconia composite using kaolin, γ-alumina and zirconia

Preparation and properties of porous mullite-based ceramics fabricated by solid state reaction

Effects of Different Aluminum Sources on Morphologies and Properties of Ceramic Floor Tiles from Red Mud

Significantly improved mechanical properties of mullite ceramics by adding AlOOH with different sizes and morphologies